PAM XIAMEN offers Silicon Ingots.
Material Description
FZ 4″Ø ingot p-type Si:B[100] ±2.0°, Ro: 1,034.10-1,853.00 Ohmcm, MCC Lifetime>1,000μs, (1 ingot: 252mm)
FZ 4″Ø×14mm p-type Si:B[100], (2,700-8,300)Ohmcm, MCC Lifetime>1,000µs
FZ 4″Ø ingot p-type Si:B[100] ±2.0°, Ro: 2,724-4,388 Ohmcm, MCC Lifetime>1,000μs, (1 ingot: 232mm)
FZ 4″Ø ingot p-type Si:B[100] ±2°, Ro: 7,200-9,557 Ohmcm, MCC Lifetime>1,000μs, [...]
2019-03-08meta-author
PAM XIAMEN offers 8″ Silicon Wafer
8″ Silicon Wafer
P-Type
Diameter 200.00±0.5 mm
Thickness 725±50μm
Dislocation density < 10-2 cm-2
Dopant – Boron
Resistivity- 10-40 Ω.cm
Chamfer width 700-1000 μm
Orientation – (100)±0.5
single sided polishing
For more information, please visit our website: https://www.powerwaywafer.com,
send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com
Found in 1990, Xiamen Powerway Advanced Material Co., Ltd (PAM-XIAMEN) is [...]
2019-09-03meta-author
HEMTs evolved from Field Effect Transistors (FETs) are suitable for manufacturing monolithic microwave integrated circuits (MMICs).
HEMTs were initially generated to obtain high electron mobility in semiconductor devices at room temperature. The electron mobility of FETs is limited even with high doping levels, so high [...]
2022-07-25meta-author
PAM XIAMEN offers CeO2 Epi Film on YSZ.
CeO2 Film (40 nm one side) on YSZ <100> 10x10x0.5 mm
Epitaxial thin Film Composition
<100> CeO2
Epitaxial Film Thickness
40 nm +/- 10 nm
Growth method
Spin coating
Epitaxial FWHM
< 5 o
Substrate
<100>, YSZ, 10x10x0.5 mm, one side polished
CeO2 Film (40 nm one side) on YSZ [...]
2019-04-19meta-author
Light-emitting InGaN/GaN Heterojunction Bipolar Transistors
The electrical and optical characteristics of high-gain, small-area InGaN/GaN heterojunction bipolar transistors (HBTs) grown by metal-organic chemical vapor depositionon sapphire substrate are reported. The common-emitter current-voltage characteristics of a 3×10 μm2 emitter device demonstrates a current gain β = ΔIC/ΔIB = [...]
2012-12-06meta-author
PAM XIAMEN offers 3″ Silicon Wafer.
Material
Orient.
Diam.
Thck
(μm)
Surf.
Resistivity
Ωcm
Comment
n-type Si:P
[111-5° towards[110]] ±0.25°
3″
1000
P/E
>5
SEMI Prime, in hard cassettes of 6, 6 & 7 wafers
n-type Si:P
[111-5° towards[110]] ±0.25°
3″
1300
P/E
>5
SEMI Prime, hard cst
n-type Si:P
[111-0.5° towards[110]] ±0.25°
3″
1400
E/E
>5
SEMI, LaserMark, in opened hard cast
n-type Si:P
[111-2.5°] ±0.5°
3″
380
P/E
1-3
SEMI Prime
n-type Si:P
[111] ±0.5°
3″
380
P/E
1-10
SEMI Primet
n-type Si:P
[111-3.0°] ±1°
3″
381
P/E
1-20 {1.7-5.7}
SEMI Test
n-type Si:P
[111] ±0.5°
3″
570
P/P
1-10
SEMI Primet
n-type Si:Sb
[111] ±0.5°
3″
380
P/E
0.019-0.026
SEMI Prime, in Empak cassettes [...]
2019-03-06meta-author