Ba1-xSrxTiO3 Film on (Pt/Ti/SiO2/Si)

  • Home
  • News
  • Ba1-xSrxTiO3 Film on (Pt/Ti/SiO2/Si)

Ba1-xSrxTiO3 Film on (Pt/Ti/SiO2/Si)

PAM XIAMEN offers BaSrTiO3 Film on substrate.

BaSrTiO3 Film ( 400nm) on Nb.SrTiO3(wt 0.7%), 10x10x0.5mm,1sp

Ba1-xSrxTiO3 is an excellent enhanced dielectronic film grown on Nb doped SrTiO3 conductive substrate via special spin coating:

Film Sppecifications:

Chemical composition: BaSrTiO3
Film thickness:  ~ 400 nm
Crystalline:         Polycrystal
Growth Method:   Spin coating + Annealing

SubstrateSpecifications:

Nb doped SrTiO3 substrate,wt 0.7%
Resistivity:                  <0.005 ohm.cm
Orientation:                         <100>
Size:                          10×10 x 0.5 mm
Polish:                        one side polished
Surface roughness:      < 5A

For more information, please visit our website: https://www.powerwaywafer.com,
send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com

Found in 1990, Xiamen Powerway Advanced Material Co., Ltd (PAM-XIAMEN) is a leading manufacturer of semiconductor material in China.PAM-XIAMEN develops advanced crystal growth and epitaxy technologies, manufacturing processes, engineered substrates and semiconductor devices.PAM-XIAMEN’s technologies enable higher performance and lower cost manufacturing of semiconductor wafer.

With more than 25+years experiences in compound semiconductor material field and export business, our team can assure you that we can understand your requirements and deal with your project professionally.

2019-04-26

Share this post

Related Posts

PAM-XIAMEN Offers InGaP

Phosphorus-containing III-V compounds are the preferred materials for millimeter-wave and submillimeter-wave devices and circuits, optoelectronic devices, and solar cells. InGaP lattice matched to GaAs has a direct band gap of 1.9eV at room temperature, which is a highly efficient light-emitting material. We are pleased [...]

2017-10-11meta-author
Mica disk

PAM XIAMEN offers Mica disk. Pure Mica Sheet Highest Grade Mica Disks, 9.9mm diameter 10/pkg Highest Grade Mica Disks, 20mm diameter 10/pkg Highest Grade Mica Sheets, 15mm x 15mm (0.59” x 0.59″”), 0.15 to 0.177mm (0.006-0.007″”) thick, 10/pkg” Hi-Grade Mica Sheets, 15mm x 15mm [...]

2019-05-13meta-author
CVD Single Crystal Diamond

Single crystal diamond for sale from PAM-XIAMEN is grown by chemical vapor deposition (CVD), which is a method of decomposing hydrogen and hydrocarbon gas into hydrocarbon active groups at high temperature, and depositing diamond on the substrate material under certain conditions. Theoretically, the method is [...]

2019-04-19meta-author
Sc Doping in Aluminum Nitride (AlN)

Aluminum nitride (AlN) is a widely used III-V group nitride with a hexagonal wurtzite structure in the field of acoustic electronic devices. It has a large direct bandgap (bandgap of 6.2 eV), is compatible with CMOS technology, and has high thermal conductivity. In addition, [...]

2024-04-03meta-author
Reducing Surface Pits of 4H-SiC Epiwafer

PAM-XIAMEN can supply SiC epitaxial wafers, more wafer specifications please read: https://www.powerwaywafer.com/sic-wafer/sic-epitaxy.html. Although SiC epitaxial wafers exhibit excellent characteristics in high-voltage and high current devices, there are still several types of defects that have a negative impact on the electrical performance of SiC devices. Among them, [...]

2024-04-11meta-author
2″ Silicon Wafer-1

PAM XIAMEN offers 2″ Silicon Wafer. Material Orient. Diam. Thck (μm) Surf. Resistivity Ωcm Comment p-type Si:B [110] ±0.5° 2″ 279 P/E FZ >1,000 p-type Si:B [100] 2″ 300 P/E FZ 2,800-3,300 SEMI Prime, TTV<7μm p-type Si:B [100] 2″ 300 P/E FZ 2,800-3,300 SEMI Prime, TTV<7μm p-type Si:B [100] 2″ 300 P/E FZ 2,800-3,300 SEMI Prime, TTV<7μm p-type Si:B [111] ±0.5° 2″ 500 P/P FZ 5,000-6,500 SEMI Test (in unsealed cassette) p-type Si:B [111] ±0.5° 2″ 275 P/E FZ 3,000-5,000 SEMI Prime, Lifetime>2,000μs, in hard cassettes of 5 wafers p-type Si:B [111-7° towards[110]] ±0.5° 2″ 279 P/P FZ >2,000 SEMI Prime p-type Si:B [111] ±0.5° 2″ 331 P/E FZ 2,000-5,000 SEMI, Soft cst p-type Si:B [111] ±0.5° 2″ 331 P/E FZ 2,000-5,000 SEMI TEST (Scratched), Soft cst p-type Si:B [111] ±0.5° 2″ 331 P/E FZ 2,000-5,000 SEMI [...]

2019-03-07meta-author