4″ Prime Silicon Wafer

4″ Prime Silicon Wafer

PAM XIAMEN offers 4″ Prime Silicon Wafer.

Silicon wafers, per SEMI Prime,
P/P 4″Ø×300±25µm,
p-type Si:B[100]±0.5°, Ro=(5-10)Ohmcm,
TTV<10µm, Bow<40µm, Warp<40µm,
Both-sides-polished, SEMI Flats (two),
Sealed in Empak cassette.
Primary Flat: 32.5±-2.5, 110±1°。
Secondary Flat: 18±2，90°±5°

For more information, please visit our website: https://www.powerwaywafer.com,
send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com

Found in 1990, Xiamen Powerway Advanced Material Co., Ltd (PAM-XIAMEN) is a leading manufacturer of semiconductor material in China. PAM-XIAMEN develops advanced crystal growth and epitaxy technologies, manufacturing processes, engineered substrates and semiconductor devices. PAM-XIAMEN’s technologies enable higher performance and lower cost manufacturing of semiconductor wafer.

PAM-XIAMEN develops advanced crystal growth and epitaxy technologies, range from the first generation Germanium wafer, second generation Gallium Arsenide with substrate growth and epitaxy on III-V silicon doped n-type semiconductor materials based on Ga, Al, In, As and P grown by MBE or MOCVD, to the third generation: Silicon carbide and Gallium Nitride for LED and power device application.

2019-07-02

Share this post

Related Posts

Test grade silicon wafers-8

PAM XIAMEN offers test grade silicon wafers Below is just a short list of the test grade silicon substrates! Inches Cust class Dopant Type Orientation PFL length PFL direction SFL Off orientation Resistivity Diameter Thickness Bow TTV Warp 6 SSP Boron P 100 57,5 ± 2,5 110 ± 0,20 0.0 ± 0.2 ° 1 – 10 Ohmcm 150.0 ± 0.2 mm 600 ± 5 µm 3 6 SSP Boron P 111 0,0 ± 0,0 110 ± 1 0.0 ± 0.2° 25 – [...]

2019-02-25meta-author
Silicon Crystal Orientation

The Silicon crystal orientations that we often hear are <100>, <110> and <111>(shown as Fig. 1), respectively indicating a crystallographic family. The single crystal silicon structure belongs to cubic crystals, and the <100> crystal orientation family represents six crystal orientations: [100], [010], [001], [100], [0-10], and [...]

2024-02-23meta-author
P Type Boron Doped Silicon Epitaxial Wafer

At present, P-P+ (boron doped) silicon epitaxial wafers are widely used in the manufacture of large-scale integrated circuits and discrete devices. The requirements for the thickness of P-P+ silicon epitaxial wafers vary with the device type. For making high-speed digital circuits, only about 0.5μm [...]

2022-12-08meta-author
1060nm High Power Laser Wafer

InGaAs quantum well (QW), as a commonly used two-dimensional material in near-infrared band, has important applications in semiconductor lasers, solar cells and other devices. In the field of semiconductor lasers, InGaAs/GaAs quantum well expands the luminous wavelength of GaAs (0.85~1.1 μm) and is widely [...]

2022-10-28meta-author
DyScO3/GdScO3//TbScO3 crystal

PAM XIAMEN offers DyScO3/GdScO3//TbScO3 crystal. Crystal  Structure /Lattice Constant(A) MP oC Density, g/cm3 Growth Tech  DyScO3  Orthorombic   a=5.44  b=5.71  c=7.89  2127  6.9  CZ  GdScO3  Orthorombic  a=5.45  b=5.75  c=7.93  2127  6.6  CZ TbScO3 Orthorhombic, a = 5.4543, b = 5.7233  c = 7.9147 2127  6.6 CZ   DyScO3 (110) 5x5x0.5mm 1sp (PAM210322-DYSCO3) DyScO3 (110) 5x5x0.5mm 1sp” DyScO3 (110) 5x5x0.5mm 2sp DyScO3 (110) 10x10x0.5mm 1sp DyScO3 (110) 10x10x0.5mm 2sp DyScO3 (001) 10x10x0.5mm 1sp [...]

2019-05-20meta-author
Something about Wafer Etching You Should Know

Etching is a technique used for micromachining to chemically remove layers from the surface of a wafer during manufacturing. Etching techniques can be divided into wet etching and dry etching. PAM-XIAMEN can provide silicon etching wafer for your applications. 1. Wet Chemical Etching The mechanism of [...]

2022-05-30meta-author