PAM XIAMEN offers Aluminum Oxide Substrate Al2O3.
Aluminum Oxide Ceramic Substrates Porperties
Purity (wt%)
0.96
0.996
0.996
0.999
Density (g/cm3)
> 3.75
3.88
3.87
3.92
Thermal conductivity (W/m. K)
24
34.7
35
35
Thermal Expansion (x10-6/oC)
< 7.7
7~8.3
7~8.3
8.1
Dielectric Strength (Kv/mm)
> 14
23.64
23.64
8.7
Dielectric Constant (at 1MHZ)
9.8
9.9
9.9
9.8
Loss Tangent (x10-4 @1MHZ)
4
1
1
< 1
Volume Resistivity (ohm-m)
> 1013 at [...]
2019-04-18meta-author
PAM XIAMEN offers 2″CZ Prime Silicon Wafer-2
2″ Silicon Wafer
Resistivity 1-5Ωcm
P type, Boron doped
Orientation (100)
Thickness 300±25μm
SSP
SEMI Prime, 1Flat, Hard cst
For more information, send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com
2020-06-11meta-author
For single photon detection technology, in addition to the traditional InP/InGaAs SPAD, new material systems such as low noise material systems constructed from Sb based digital alloys, multi multiplication InP/InGaAs SPAD using ionization engineering, and InAlAs/InGaAs SPAD have also been developed. PAM-XIAMEN can provide InP [...]
2023-07-12meta-author
PAM XIAMEN offers 4″ FZ silicon ignot.
Silicon ingot, per SEMI, G 100.7±0.3mmØ,
FZ Intrinsic undoped Si:-[111]±2.0°, Ro > 25,000 Ohmcm,
Ground Ingot, NO Flats,
MCC Lifetime>1000µs.
NOTE: Oxygen<1E16/cc, Carbon<1E16/cc,
For more information, please visit our website: https://www.powerwaywafer.com,
send us email at sales@powerwaywafer.com and [...]
2019-07-02meta-author
PAM XIAMEN offers Fe – Stainless Steel Substrate ( Polycrystaline).
Stainless Steel Substrate (SUS301 HV200-HV600 ): 1″ Dia x 0.3 mm, as cold rolling
Stainless Steel Foil: SS316 0.1mm Thick x 300mm W x 4000 mm L
Stainless Steel Foam: SS316 1mm Thick x [...]
2019-05-08meta-author
GaN Power Electronics will top one billion dollar in revenue in a couple of years thanks to a cross-fertilization with the LED industry
SLOW RAMP-UP BUT HUGE EXPECTATIONS
The GaN power device industry has probably generated less than $2.5M revenues in 2011, as only 2 companies are selling [...]