PAM XIAMEN offers test grade silicon wafers
Below is just a short list of the test grade silicon substrates!
Inches | Cust class | Dopant | Type | Orientation | PFL length | PFL direction | SFL | Off orientation | Resistivity | Diameter | Thickness | Bow | TTV | Warp |
6 | SSP | Boron | P+ | 100 | 57,5 ± 2,5 | 100 ± 1 | 0.0 ± 5.0 ° | 0.001 – 100 Ohmcm | 150 ± 0.5 mm | 675 ± 200 µm | 100 | 20 | 100 | |
6 | SSP | Boron | P | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5 ° | > 0.3 Ohmcm | 150 ± 0.5 mm | 400 ± 50 µm | 60 | 30 | 60 | |
6 | SSP | Boron | P+ | 100 | 47,5 ± 2,5 | 110 ± 1 | 0.0 ± 1° | 0.010 – 0.020 Ohmcm | 150 ± 0.5 mm | 508 ± 15 µm | 60 | |||
6 | SSP | Phosphorus | N | 111 | 57,5 ± 2,5 | 110 ± 1 | 4.0 ± 1.0 ° | 4 – 8 Ohmcm | 150 ± 0.2 mm | 650 ± 50 µm | 60 | 10 | 60 | |
6 | SSP | Phosphorus | N | 111 | 57,5 ± 2,5 | 110 ± 1 | 4.0 ± 1.0 ° | 0.75 – 5.00 Ohmcm | 150 ± 0.2 mm | 675 ± 25 µm | 10 | 50 | ||
6 | SSP | Phosphorus | N | 111 | 57,5 ± 2,5 | 110 ± 1 | 4.0 ± 1.0 ° | 0.75 – 5.00 Ohmcm | 150 ± 0.2 mm | 675 ± 25 µm | ||||
6 | SSP | Antimony | N+ | 100 | 47,5 ± 2,5 | 011 ± 1 | 0.0 ± 1.0° | 0.008 – 0.016 Ohmcm | 150 ± 0.5 mm | 550 ± 15 µm | ||||
6 | SSP | Antimony | N+ | 100 | 47,5 ± 2,5 | 011 ± 1 | 0.0 ± 1.0° | 0.008 – 0.016 Ohmcm | 150 ± 0.5 mm | 400 ± 15 µm | ||||
6 | SSP | Antimony | N+ | 100 | 0,0 ± 0,0 | 110 ± 1 | 4° towards [110] ± 0.5° | 0.005-0.030 Ohmcm | 150 ± 0.2 mm | 1000 ± 20 µm | 50 | 50 | ||
6 | SSP | Antimony | N+ | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5 ° | 0.01 – 0.025 Ohmcm | 150 ± 0.5 mm | 1000 ± 30 µm | 8 | |||
6 | SSP | Antimony | N+ | 111 | 57,5 ± 2,5 | 110 ± 1 | 4.0 ± 0.5 ° | 0.01 – 0.02 Ohmcm | 150 ± 0.5 mm | 625 ± 15 µm | 30 | |||
6 | SSP | Antimony | N+ | 100 | 47,5 ± 2,5 | 110 ± 1 | 0.0 ± 1.0° | 0.01 – 0.020 Ohmcm | 150 ± 0.5mm | 625 ± 10 µm | 40 | 5 | 40 | |
6 | SSP | Antimony | N+ | 111 | 57,5 ± 2,5 | 011 ± 1 | 3.0 ± 0.5° | < 0.016 Ohmcm | 150 ± 0.3 mm | 300 ± 15 µm | 25 | 10 | 60 | |
6 | SSP | Antimony | N+ | 100 | 0,0 ± 0,0 | 110 ± 1 | 1° towards [110] ± 0.25° | 0.005-0.030 Ohmcm | 150 ± 0.2 mm | 750 ± 10 µm | 50 | 50 | ||
6 | SSP | Antimony | N+ | 100 | 0,0 ± 0,0 | 110 ± 1 | 4° towards [110] ± 0.25° | 0.005-0.030 Ohmcm | 150 ± 0.2 mm | 750 ± 10 µm | 50 | 50 | ||
6 | SSP | Antimony | N+ | 100 | 57,5 ± 2,5 | 110 ± 1 | 0.0 ± 1.0 ° | 0.005 – 0.020 Ohmcm | 150 ± 0.2 mm | 625 ± 15 µm | ||||
6 | SSP | Antimony | N+ | 111 | 57,5 ± 2,5 | 110 ± 1 | 3.0 ± 0.5 ° | 8 – 17 mOhmcm | 150.0 ± 0.2 mm | 625 ± 15 µm | 40 | 10 | 40 | |
6 | SSP | Antimony | N+ | 100 | 0,0 ± 0,0 | 110 ± 1 | 2° towards [110] ± 0.5° | 0.005-0.030 Ohmcm | 150 ± 0.2 mm | 1000 ± 10 µm | 50 | 50 | ||
6 | SSP | Antimony | N+ | 100 | 57,5 ± 2,5 | 110 ± 0,30 | 0.0 ± 0.5° | 0.005 – 0.020 Ohmcm | 150.0 ± 0.2 mm | 675 ± 15 µm | 20 | 5 | 35 | |
6 | SSP | Antimony | N+ | 111 | 57,5 ± 2,5 | 011 ± 1 | 3.0 ± 0.5° | < 0.016 Ohmcm | 150 ± 0.3 mm | 300 ± 15 µm | 25 | 10 | 60 | |
6 | SSP | Antimony | N+ | 100 | 57,5 ± 2,5 | 110 ± 1 | 135 ± 5° °, 20 ± 2.5 mm | 0.0 ± 0.5° | 0.005 – 0.020 Ohmcm | 150 ± 0.5 mm | 525 ± 25 µm | 50 | 5 | 50 |
6 | SSP | Antimony | N+ | 100 | 57,5 ± 2,5 | 110 ± 1 | 0.0 ± 1.0° | 0.005 – 0.020 Ohmcm | 150 ± 0.2 mm | 625 ± 15 µm | 40 | 10 | 25 | |
6 | SSP | Antimony | N+ | 100 | 57,5 ± 2,5 | 110 ± 1 | 0.0 ± 1.0 ° | < 0.020 Ohmcm | 150 ± 0.2 mm | 625 ± 15 µm | 6 | 55 | ||
6 | SSP | Antimony | N+ | 100 | 57,5 ± 2,5 | 110 ± 1 | 135 ± 5.0 °, 20.00 ± 2.5 mm | 0.0 ± 0.5° | 0.005 – 0.020 Ohmcm | 150 ± 0.5 mm | 525 ± 25 µm | 38 | 12 | 38 |
6 | SSP | Antimony | N+ | 100 | 47,5 ± 2,5 | 110 ± 1 | 0.0 ± 1.0° | 0.01 – 0.020 Ohmcm | 150 ± 0.5mm | 625 ± 10 µm | ||||
6 | SSP | Antimony | N+ | 100 | 0,0 ± 0,0 | 110 ± 1 | 1° towards [110] ± 0.25° | 0.005-0.030 Ohmcm | 150 ± 0.2 mm | 1000 ± 10 µm | ||||
6 | SSP | Antimony | N+ | 100 | 57,5 ± 2,5 | 110 ± 0,30 | 0.0 ± 0.5° | 0.005-0.020 Ohmcm | 150.0 ± 0.2 mm | 665-685 µm | ||||
6 | SSP | Antimony | N+ | 100 | 47,5 ± 2,5 | 011 ± 1 | 0.0 ± 0.5° | 0.008 – 0.020 Ohmcm | 150 ± 0.5 mm | 625 ± 15 µm | 4,5 | 50 | ||
6 | SSP | Antimony | N+ | 100 | 57,5 ± 2,5 | 110 ± 1 | 0.0 ± 1.0 ° | < 0.020 Ohmcm | 150 ± 0.2 mm | 625 ± 15 µm | ||||
6 | SSP | Arsenic | N+ | 111 | 47,5 ± 2,5 | 110 ± 1 | 2.5 ± 0.5 ° | <0.003 Ohmcm | 150 ± 0.5 mm | 625 ± 25 µm | 60 | 15 | 60 | |
6 | SSP | Arsenic | N+ | 111 | 47,5 ± 2,5 | 110 ± 1 | 2.5 ± 0.5 ° | <0.004 Ohmcm | 150 ± 0.5 mm | 625 ± 25 µm | 60 | 8 | 60 | |
6 | SSP | Arsenic | N+ | 111 | 57,5 ± 2,5 | 011 ± 1 | 3.0 ± 0.5 ° | 1 – 4 mOhmcm | 150 ± 0.2 mm | 625 ± 15 µm | 10 | 40 | ||
6 | SSP | Arsenic | N+ | 100 | 47,5 ± 1,0 | 110 ± 0,50 | 0.0 ± 0.5° | 0.003 – 0.004 Ohmcm | 150.0 ± 0.2 mm | 625 ± 15 µm | 30 | 10 | 30 | |
6 | SSP | Arsenic | N+ | 111 | 47,5 ± 2,5 | 110 ± 1 | 2.5 ± 0.5 ° | 0.002 – 0.004 Ohmcm | 150 ± 0.2 mm | 625 ± 15 µm | 30 | 5 | 45 | |
6 | SSP | Arsenic | N+ | 111 | 57,5 ± 2,5 | 011 ± 1 | 3.0 ± 0.5 ° | 1 – 4 mOhmcm | 150 ± 0.2 mm | 625 ± 15 µm | 10 | 40 | ||
6 | SSP | Arsenic | N+ | 111 | 57,5 ± 2,5 | 011 ± 1 | 3.0 ± 0.5 ° | 1 – 4 mOhmcm | 150 ± 0.2 mm | 625 ± 15 µm | 10 | 40 | ||
6 | SSP | Arsenic | N+ | 100 | 57,5 ± 2,5 | 110 ± 1 | 0.0 ± 1.0 ° | 0.003 – 0.005 Ohmcm | 150.0 ± 0.2 mm | 625 ± 15 µm | 15 | 60 | ||
6 | SSP | Arsenic | N+ | 100 | 57,5 ± 2,5 | 110 ± 1 | 0.0 ± 1.0 ° | 0.003 – 0.005 Ohmcm | 150 ± 0.2 mm | 625 ± 15 µm | 15 | 60 | ||
6 | SSP | Arsenic | N+ | 111 | 57,5 ± 2,5 | 110 ± 1 | 4.0 ± 1.0° | 0.0020-0.0026 Ohmcm | 150 ± 0.25 mm | 508 ± 15 µm | 15 | 40 | ||
6 | SSP | Arsenic | N+ | 111 | 57,5 ± 2,5 | 110 ± 1 | 4.0 ± 0.5 ° | < 0.0035 Ohmcm | 150 ± 0.7 mm | 440 ± 20 µm | 90 | 17 | 90 | |
6 | SSP | Arsenic | N+ | 111 | 57,5 ± 2,5 | 110 ± 1 | 4.0 ± 1.0° | 0.0020-0.0026 Ohmcm | 150 ± 0.25 mm | 508 ± 15 µm | 15 | 40 | ||
6 | SSP | Arsenic | N+ | 111 | 0,0 ± 0,0 | 110 ± 1 | 2.5 ± 0.5 ° | <0.006 Ohmcm | 150 ± 0.5 mm | 675 ± 25 µm | 60 | 15 | 60 | |
6 | SSP | Arsenic | N+ | 111 | 57,5 ± 2,5 | 110 ± 1 | 4.0 ± 0.5 ° | < 0.0035 Ohmcm | 150 ± 0.7 mm | 440 ± 20 µm | 90 | 17 | 90 | |
6 | SSP | Arsenic | N+ | 111 | 57,5 ± 2,5 | 011 ± 1 | 3.0 ± 0.5 ° | 1 – 4 mOhmcm | 150 ± 0.2 mm | 625 ± 15 µm | 10 | 40 | ||
6 | SSP | Arsenic | N+ | 100 | 47,5 ± 1,0 | 110 ± 0,50 | 0.0 ± 0.5° | 0.002 – 0.003 Ohmcm | 150.0 ± 0.2 mm | 625 ± 15 µm | 30 | 10 | 30 | |
6 | SSP | Arsenic | N+ | 100 | 47,5 ± 1,0 | 110 ± 0,50 | 0.0 ± 0.5° | 0.003 – 0.004 Ohmcm | 150.0 ± 0.2 mm | 625 ± 15 µm | 30 | 10 | 30 | |
6 | SSP | Arsenic | N+ | 100 | 57,5 ± 2,5 | 110 ± 1 | 0.0 ± 1.0° | 0.003 – 0.008 Ohmcm | 150 ± 0.5 mm | 380 ± 15 µm | 45 | 5 | 45 | |
6 | SSP | Arsenic | N+ | 111 | 0,0 ± 0,0 | 110 ± 1 | 2.5 ± 0.5 ° | <0.006 Ohmcm | 150 ± 0.5 mm | 675 ± 25 µm | 60 | 15 | 60 | |
6 | SSP | Arsenic | N+ | 111 | 57,5 ± 2,5 | 110 ± 1 | 4.0 ± 1.0° | 0.0020-0.003 Ohmcm | 150 ± 0.25 mm | 508 ± 15 µm | 15 | 40 | ||
6 | SSP | Arsenic | N+ | 100 | 47,5 ± 2,5 | 0TT ± 1 | 0.0 ± 1.0 ° | < 0.0035 Ohmcm | 150.0 ± 0.2 mm | 625 ± 25 µm | 6 | 40 | ||
6 | SSP | Arsenic | N+ | 111 | 57,5 ± 2,5 | 110 ± 1 | 4.0 ± 1.0° | 0.0020-0.0026 Ohmcm | 150 ± 0.25 mm | 508 ± 15 µm | 15 | 40 |
For more information, please visit our website: https://www.powerwaywafer.com,
send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com
Found in 1990, Xiamen Powerway Advanced Material Co., Ltd (PAM-XIAMEN) is a leading manufacturer of semiconductor material in China.PAM-XIAMEN develops advanced crystal growth and epitaxy technologies, manufacturing processes, engineered substrates and semiconductor devices.PAM-XIAMEN’s technologies enable higher performance and lower cost manufacturing of semiconductor wafer.
You can get our free technology service from enquiry to after service based on our 25+ experiences in semiconductor line.