Oblea de silicio de 2 ″-10

Oblea de silicio de 2 ″-10

PAM XIAMEN ofrece oblea de silicio de 2 ″.

Material Orientar. Diám. grueso
(μm)		 Navegar. Resistividad
Ωcm		 Comentario
tipo n Si:P [111] 2″ 300 PÁGINAS ZF >150 SEMI Prime
tipo n Si:P [111] 2″ 500 PÁGINAS ZF 130-150 SEMI Prime
tipo n Si:P [111] 2″ 300 PÁGINAS ZF 125-210 SEMI Prime
tipo n Si:P [111] 2″ 380 EDUCACIÓN FÍSICA ZF 100-300 SEMI Prime
tipo n Si:P [111] 2″ 450 PÁGINAS FZ 100-230 Prime, NO pisos
tipo n Si:P [111] ±0,5° 2″ 280 EDUCACIÓN FÍSICA FZ NTD 80-100 SEMI Prime, en cst duro {como lingote para procesar}
tipo n Si:P [111] 2″ 300 PÁGINAS FZ 70-95 SEMI Prime
tipo n Si:P [111-1°] 2″ 300 EDUCACIÓN FÍSICA Ley Federal 69-77 SEMI Prime
tipo n Si:P [111] 2″ 300 PÁGINAS ZF >60 SEMI Prime
tipo n Si:P [111] 2″ 300 EDUCACIÓN FÍSICA FZ 60-90 SEMI Prime
tipo n Si:P [111] ±0,5° 2″ 280 EDUCACIÓN FÍSICA FZ NTD 55-75 SEMI Prime, en cst duro {como lingote para procesar}
tipo n Si:P [111] 2″ 280 ENERGÍA FZ 40-50 SEMI Prime
tipo n Si:P [111] ±0,5° 2″ 280 EDUCACIÓN FÍSICA FZ NTD 40-60 SEMI Prime, en cst duro {como lingote para procesar}
tipo n Si:P [111] ±0,5° 2″ 280 EDUCACIÓN FÍSICA FZ NTD 35-45 SEMI Prime, en cst duro {como lingote para procesar}
tipo n Si:P [111] 2″ 300 PÁGINAS ФЗ 15-30 SEMI Prime
tipo n Si:P [111] 2″ 500 PÁGINAS ФЗ 10-55 SEMI Prime
tipo n Si:P [111] ±0,5° 2″ 300 EDUCACIÓN FÍSICA FZ NTD 7-8 SEMI
Si intrínseco:- [100] 2″ 475 EDUCACIÓN FÍSICA Zona franca >10.000 SEMI Prime
Si intrínseco:- [100-4,0°] ±0,5° 2″ 350 EDUCACIÓN FÍSICA ZF > 3.000 SEMI Prime, TTV<5μm
Si intrínseco:- [111] ±0,5° 2″ 330 PÁGINAS Zona franca >20.000 SEMI
Si intrínseco:- [111] ±0,5° 2″ 300 EDUCACIÓN FÍSICA 1.000-20.000 libras esterlinas SEMI Prime

Para obtener más información, por favor visite nuestro sitio web:https://www.powerwaywafer.com,
envíanos un correo electrónico aventas@powerwaywafer.comypowerwaymaterial@gmail.com

Fundada en 1990, Xiamen Powerway Advanced Material Co., Ltd (PAM-XIAMEN) es un fabricante líder de material semiconductor en China. PAM-XIAMEN desarrolla tecnologías avanzadas de epitaxia y crecimiento de cristales, procesos de fabricación, sustratos de ingeniería y dispositivos semiconductores. Las tecnologías permiten un mayor rendimiento y un menor coste de fabricación de obleas semiconductoras.

Puede obtener nuestro servicio de tecnología gratuito desde la consulta hasta el servicio posventa basado en nuestras más de 25 experiencias en la línea de semiconductores.

2019-03-07

Compartir esta publicacion

RelacionadoPublicaciones

LD Bare Bar for 808nm@cavity 2mm

PAM XIAMEN offers LD Bare Bar for 808nm@cavity 2mm. Brand: PAM-XIAMEN Wavelength: 808nm Filling Factor: 38% Output Power: 100W Cavity Length:2mm For more information, please visit our website: https://www.powerwaywafer.com, send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com Found in 1990, Xiamen Powerway Advanced Material Co., [...]

2019-05-09metaautor
4″ Silicon Wafer-8

PAM XIAMEN offers 4″ Silicon Wafer. Material Orient. Diam. Thck (μm) Surf. Resistivity Ωcm Comment p-type Si:B [100] 4″ 2100 P/E 1-100 SEMI Prime, Manual Edges p-type Si:B [100] 4″ 3000 P/P 1-10 SEMI Prime p-type Si:B [100] 4″ 3175 P/P 1-10 SEMI Prime, TTV<8μm p-type Si:B [100] 4″ 3200 P/E 1-100 SEMI Prime, Sealed as group of 9 wafers p-type Si:B [100] 4″ 4000 P/P 1-100 SEMI Prime p-type Si:B [100] 4″ 4000 P/P 1-100 SEMI Prime p-type Si:B [100] 4″ 5000 P/E 1-100 Prime, NO Flats p-type Si:B [100] 4″ 890 ±15 P/P 0.5-10.0 SEMI TEST (Scratches), TTV<8μm p-type Si:B [100] ±0.2° 4″ 300 P/P 0.1-0.3 SEMI Prime p-type Si:B [100] ±1° 4″ 490 ±5 P/P 0.1-1.0 SEMI Prime, TTV<0.8μm p-type Si:B [100] 4″ 525 P/E 0.1-0.2 SEMI Prime p-type Si:B [100] 4″ 350 P/E 0.095-0.130 SEMI Prime p-type [...]

2019-03-05metaautor
Semi-insulating GaAs Substrate

PAM-XIAMEN offers 4inch Semi-insulating GaAs Substrate with good flatness such as TTV<=3UM, BOW<=4um, and WARP<5um, TIR(Total Indicated Runout)<=3um, LFPD(Local Focal Plane Deviation)<=1um, LTV(Local Thickness Variation)<=1.5um, which can be used for Microelectronic application. 1. Specification of Semi-insulating GaAs Substrate 1.1 Semi-insulated GaAs Substrate PAM190425-GAAS Parameter Customer’sRequirements Guaranteed/Actual Values UOM GrowthMethod: VGF VGF — ConductType:. S-I-N S-I-N — Dopant: c doped c [...]

2020-05-26metaautor
(20-21) Plane Si-GaN Freestanding GaN Substrate

PAM-XIAMEN offers (20-21) Plane Si-GaN Freestanding GaN Substrate Item PAM-FS-GAN(20-21)-SI Dimension 5 x 10 mm2 or 5 x 20 mm2 Thickness 380+/-50um Orientation (20-21)/(20-2-1) plane off angle toward A-axis 0 ±0.5° (20-21)/(20-2-1) plane off angle toward C-axis -1 ±0.2° Conduction Type Semi-Insulating Resistivity (300K) > 106 Ω.cm TTV ≤ 10 µm BOW BOW ≤ 10 µm Surface Roughness: Front side: Ra<0.2nm, epi-ready; Back side: Fine Ground or polished. Dislocation Density ≤5 x 106 cm-2 Macro Defect Density 0 cm-2 Useable Area > 90% (edge exclusion) Package each in single wafer container, under nitrogen atmosphere, packed in class 100 clean room   For more information, please contact us email at victorchan@powerwaywafer.com and powerwaymaterial@gmail.com

2020-08-20metaautor
10*10 mm2 N-GaN Freestanding GaN Substrate

PAM-XIAMEN, one of leading GaN substrate manufacturers, offers 10*10mm2 N-Type Freestanding GaN Substrate. To get more specific information please see the table below: 1. N-Type Freestanding GaN Substrate Specification Item PAM-FS-GAN-50-N Dimension 10 x 10.5 mm2 Thickness 380+/-50um Orientation C plane (0001) off angle toward M-axis 0.35 ±0.15° Conduction Type N-type / Si Doped Resistivity (300K) < 0.05 Ω·cm TTV ≤ 10 µm BOW BOW ≤ 10 µm Surface Roughness: Front side: Ra<0.2nm, epi-ready; Back side: Fine Ground or polished. Dislocation Density ≤5x 106 cm-2 (calculated by CL)* Macro Defect Density 0 cm-2 Useable Area > 90% (edge exclusion)   Package each in single wafer container, under nitrogen atmosphere, packed in [...]

2020-08-17metaautor
1″ Silicon Wafer-2

PAM XIAMEN offers 1″ Silicon Wafer. Material Orient. Diam. Thck (μm) Surf. Resistivity Ωcm Comment p-type Si:B [111] ±0.5° 1″ 50 ±10 P/P 1-100 n-type Si:P [100] 1″ 50 ±10 P/P >20 SEMI Prime, TTV<5μm, in single wafer trays between clean-room sheets, MOQ 4 wafers n-type Si:P [100] 1″ 280 P/P 1-20 SEMI Prime n-type Si:P [100] 1″ 280 P/E 1-5 SEMI n-type Si:P [100] 1″ 1500 P/E 1-20 Prime, n-type Si:P [100] 1″ 525 P/E 0.05-0.15 SEMI n-type Si:P [111] 1″ 330 P/E FZ >90 Prime p-type Si:B [100] 1″ 775 P/E 8-12 SEMI Prime p-type Si:B [100] 24mm 300 P/E 1-100 Prime, p-type Si:B [100] 1″ 300 P/E 1-10 Prime, p-type Si:B [100] 1″ 500 P/E 1-10 p-type Si:B [100] 1″ 380 P/E 0.003-0.005 SEMI Prime p-type Si:B [100] 1″ 275 P/E 0.002-0.005 Prime n-type Si:P [100] 1″ 50 ±10 P/P >20 SEMI Prime, TTV<5μm, in single wafer trays [...]

2019-03-08metaautor