PAM XIAMEN offers 4″ FZ Intrinsic Silicon Wafer SSP
4″ FZ (100) intrinsic, SSP
wafer Si FZ (100)
dia 4’’ x 525µm
intrinsic
R > 20,000 ohm.cm
one side polished with SEMI Std flats
Roughness<0.5nm
For more information, send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com
2021-03-17meta-autor
PAM XIAMEN offers 4″FZ Prime Silicon Wafer.
4″ Si wafer, R>20,000Ωcm
Silicon, Si wafers
orientation (100)
dimensions 100 mm x 525µm (+/-25µm) thick.
FZ >20 000 ohm.cm
Ra<0.5 nm
One side polished
Ra<0.5nm (µelectronic grade)
For more information, please visit our website: https://www.powerwaywafer.com,
send [...]
2019-07-05meta-autor
PAM XIAMEN offers Nickel Single crystal.
tomic number: 28
Atomic number: 28
Atomic mass: 58.71 g.mol -1
Atomic mass: 58.71 g.mol -1
Crystal structure: F.C.C
Crystal structure: F.C.C
Lattice Constant: 0.325 nm
Lattice Constant: 0.325 nm
Ni Single crystal
Ni Single Crystal Substrate, <100>, 10 x 5 x 0.5 mm, 1 side polished
Ni Single Crystal Substrate, <100>, 10×10 x [...]
2019-05-13meta-autor
For single photon detection technology, in addition to the traditional InP/InGaAs SPAD, new material systems such as low noise material systems constructed from Sb based digital alloys, multi multiplication InP/InGaAs SPAD using ionization engineering, and InAlAs/InGaAs SPAD have also been developed. PAM-XIAMEN can provide InP [...]
2023-07-12meta-autor
PAM XIAMEN offers LaSrAlO4 Strontium Lanthanum Aluminate Crystal Substrates.
Main Parameters
Crystal structure
M4
Growth method
Czochralski method
Unit cell constant
a=3.756Å c=12.63 Å
Melt point(℃)
1650
Density
5.92(g/cm3)
Hardness
6-6.5(mohs)
Dielectric constants
ε=16.8
Size
10×3,10×5,10×10,15×15,20×15,20×20
Ф15, Ф20,Ф1″,Ф2″, Ф2.6″
Thickness
0.5mm, 1.0mm
Polishing
Single or [...]
2019-03-13meta-autor
PAM XIAMEN offers Si wafer Thickness: 675 ± 25 um.
Si wafer
Method: Cz
Orientation: <111>
Type: P-Type
Dopant: Boron
Resistivity: 0.1-13 ohm.cm
Diameter: 150 ± 0.1 mm
Thickness: 675 ± 25 um
Chamfer
Front side: Epi-ready
Back side: etched
BOW < 30um
Warp [...]
2019-08-22meta-autor