Fe2O3 crystal

Fe2O3 crystal

PAM XIAMEN offers Fe2O3 crystal .

Alpha-Fe2O3 Crystal (0001) < 0.4deg, Edge oriented, 5x5x1.0mm,1SP

Specifications:
Crystal:                    Alpha-Fe2O3 natural source with defects
Purity:                      >99.95%
Size:                        5  mm x 5 mm x 1.0 mm
Orientation:              (0001) < 0.4 degree
Edge:                      (11-20) (1-100)
Polishing:                single  side polished
Surface roughness:  Ra <10 nm

Alpha-Fe2O3 crystal (0001) <0.4 deg, 10x10x0.5 mm, 1SP

Specifications:
Crystal:                   Fe2O3 natural source with defects
Purity:                     >99.95%
Size:                      10 mm x 10 mm x 0.5 mm
Orientation:             (0001) <0.4 deg
Edge Orienation:      <11-20>
Polishing:               single  side polished
Surface roughness: Ra < 10 nm

Alpha-Fe2O3 Crystal (1-100) <0.4deg, Edge oriented, 5x5x1.0mm,1SP

Specifications:
Crystal:                  Alpha-Fe2O3 natural source with defects
Purity:                    >99.95%
Size:                      5 mm x 5 mm x 1.0 mm
Orientation:             (1-100) < 0.4 degree
Edge:                     (0001) (11-20)
Polishing:               single side polished
Surface roughness: Ra <10 nm

Alpha-Fe2O3 Crystal (11-20) <0.4deg, Edge oriented ,5x5x1.0mm,1SP

Specifications:
Crystal:                    Alpha-Fe2O3 natural source with defects
Size:                        5 mm x 5 mm x 1.0 mm
Orientation:              (11-20) < 0.4 degree
Edge:                      (0001) (1-100)
Polishing:                single  side polished
Surface roughness:  Ra <10 nm

Typical Properties

Crystal growth method Natural
Crystal orientation (0001) (1010) (1120) others on request
Maximum size up to 20 x 20 mm
Crystallographic properties a = 5.04 A, c = 13.77 A
Crystallographic structure hexagonal
Twinning structure natural defects
Colour black
Density 5.20 g/cm³
Hardness 6.5

For more information, please visit our website: https://www.powerwaywafer.com,
send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com

Found in 1990, Xiamen Powerway Advanced Material Co., Ltd (PAM-XIAMEN) is a leading manufacturer of semiconductor material in China. PAM-XIAMEN develops advanced crystal growth and epitaxy technologies, manufacturing processes, engineered substrates and semiconductor devices. PAM-XIAMEN’s technologies enable higher performance and lower cost manufacturing of semiconductor wafer.

You can get our free technology service from enquiry to after service based on our 25+ experiences in semiconductor line.

2019-04-19

Share this post

Related Posts

The effect of GaN and ain buffer layers on GaN film properties grown on both C-plane and A-plane sapphire

The effect of GaN and ain buffer layers on GaN film properties grown on both C-plane and A-plane sapphire   This paper presents a comparative study of the properties of GaN grown by organometallic vapor phase epitaxy, using both a GaN and A1N buffer layer, as [...]

2013-04-03meta-author
Undoped InP Wafer

Undoped InP Wafer PAM-XIAMEN offer low doped InP wafer substrate, see the following: InP wafer,2”  (PAM-190507-INP) Diameter – 50.8±0.5 mm; Thickness – 350±25 µm; N type, low doped Dopant – low doped Orientation – (100)±0.5° Flat orientation – SEMI-E/J; Major flat orientation – (0-1-1) ±0.5° Major flat length – 16.0±1.0 mm; [...]

2020-03-18meta-author
SrTiO3 single crystal-1

PAM XIAMEN offers SrTiO3 single crystal. SrTiO3 (STO) single crystal provides a good lattice match to most of  materials with Perovskite structure.  It is an excellent substrate for epitaxial film of HTS and many oxide. It has been used widely for special optical windows and as high quality [...]

2019-05-14meta-author
Silicon Epi Wafers Sale

Silicon Epi Wafers Sale PAM XIAMEN offers Silicon Epi Wafers.       6″ Epitaxial Silicon Wafers Item Substrate EPI Comment Size Type Res Ωcm Surf. Thick μm Type Res Ωcm PAM3197 6″Øx675μm n- Si:P[100] 0.001-0.002 P/EOx 0.016 n- Si:P 0.32-0.46 n/n+ 4″ Epitaxial Silicon Wafers Item Substrate EPI Comment Size Type Res Ωcm Surf. Thick μm Type Res Ωcm PAM3198 4″Øx360μm n- Si:Sb[111] 0.005-0.020 P/E 20 n- Si:P 360 – 440 n/n+ PAM3199 4″Øx400μm p- Si:B[111] 0.01-0.10 P/E 6.5 p- Si:B 3.6±10% P/P/P+ 22±1.5 p- Si:B 300±50 PAM3200 4″Øx525μm p- Si:B[111] 0.01-0.02 P/E 8.1±1 p- Si:B 4.5±10% P/P/P+ 6.85±0.75 p- Si:B 0.75±0.15 PAM3201 4″Øx380μm p- Si:B[111] 0.008-0.020 P/EOx 10.5 p- Si:B 570±10% p/p+ PAM3202 4″Øx440μm p- Si:B[111] 0.008-0.020 P/E 20 p- Si:B 0.15 ±10% P/P+ PAM3203 4″Øx440μm p- Si:B[111] 0.008-0.020 P/E 20 p- Si:B 0.25±10% P/P+ PAM3204 4″Øx525μm p- Si:B[111] 0.001-0.005 P/E 20 p- Si:B 175±10% P/P+ PAM3205 4″Øx440μm p- Si:B[111] 0.008-0.020 P/E 21 p- Si:B 150 [...]

2019-02-15meta-author
Ce:Lu2SiO5 substrate

PAM XIAMEN offers Ce:Lu2SiO5 substrate. Ce:Lu2SiO5 substrate (001 ) 10x10x0.5 mm, 1sp Substrate Specifications Crystal:             Ce: Lu2SiO5 Ce dopant          0.175 mol % Size:                 10x10x0.5 mm   Orientation:        (001 ) +/-0.5 0 Polish:               One side optical polished. Ce:Lu2SiO5 substrate (001) 10x10x0.5 mm, 2sp [...]

2019-05-08meta-author
From graphene to silicon carbide: ultrathin silicon carbide flakes

This study presents a new ultrathin SiC structure prepared by a catalyst free carbothermal method and post-sonication process. We have found that merging ultra-light 3D graphene foam and SiO together at high temperature leads to the formation of a complex SiC structure consisting of [...]

2019-01-09meta-author