1″&1.5″ Silicon Wafer

1″&1.5″ Silicon Wafer

PAM XIAMEN offers 1″&1.5″ Silicon Wafer.

Diameter Type Dopant Growth
method		 Orientation Resistivity  Thickness Surface Grade
25.4 N Phos CZ -100 1-20 43768 P/P PRIME
25.4 N Phos CZ -100 1-20 40-60 P/P PRIME
25.4 N Phos CZ -100 1-20 80-100 P/P PRIME
25.4 N Phos CZ -100 1-20 140-160 P/P PRIME
25.4 N Phos CZ -100 225-275 P/P PRIME
25.4 N Phos CZ -100 225-275 P/P PRIME
25.4 N Phos CZ -100 250-300 P/E PRIME
25.4 N Phos CZ -100 250-300 P/E PRIME
25.4 P Boron CZ -100 1-20 43768 P/P PRIME
25.4 P Boron CZ -100 1-20 40-60 P/P PRIME
25.4 P Boron CZ -100 1-20 80-100 P/P PRIME
25.4 P Boron CZ -100 1-20 140-160 P/P PRIME
25.4 P Boron CZ -100 1-20 225-275 P/P PRIME
25.4 P Boron CZ -100 1-20 225-275 P/P PRIME
25.4 P Boron CZ -100 1-20 250-300 P/E PRIME
25.4 P Boron CZ -100 1-20 250-300 P/E PRIME
25.4 Intrinsic Undoped FZ -100 > 20000 275-325 P/E PRIME
25.4 N Sb CZ -100 .5-40 200-250 P/E PRIME
25.4 N Sb CZ -100 5-40 225-275 P/E PRIME
25.4 Single Wafer Shipper ePak Lid/Base/Spring Holds1Wafer Clean Room
25.4 Shipping Cassette ePak Holds25Wafers Clean Room
38.1 Single Wafer Shipper ePak Lid/Base/Spring Holds1Wafer Clean Room

For more information, please visit our website: https://www.powerwaywafer.com,
send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com

Found in 1990, Xiamen Powerway Advanced Material Co., Ltd (PAM-XIAMEN) is a leading manufacturer of semiconductor material in China.PAM-XIAMEN develops advanced crystal growth and epitaxy technologies, manufacturing processes, engineered substrates and semiconductor devices.PAM-XIAMEN’s technologies enable higher performance and lower cost manufacturing of semiconductor wafer.

Our goal is to meet all of your requirements, no matter how small orders and how difficult questions they may be,
to maintain sustained and profitable growth for every customer through our qualified products and satisfying service.

2019-02-27

Share this post

Related Posts

6″ FZ Silicon Wafer-5

PAM XIAMEN offers6″ FZ Silicon Wafer-5 Silicon wafers, per SEMI Prime, P/E 6″Ø×875±25µm, FZ p-type Si:B[111]±0.5°, Ro > 10,000 Ohmcm, Warp<60μm, One-side-polished, Particles: ≤10@≥0.3μm, MCL (Na, Al, K, Fe, Ni, Cu, Zn)<5E10/cm²,back-side etched, Tarnish, orange peel, contamination, haze, micro scratch, chips, edge chips, crack, crow feet, pin hole, pits, dent, waviness, smudge&scar on [...]

2019-09-19meta-author
3″CZ Prime Silicon Wafer

PAM XIAMEN offers 3″CZ Prime Silicon Wafer Item3, 50pcs Silicon wafer: i. Diameter: 76.2 mm ± 0.5 mm, ii. Thickness: 375μm ±25μm iii. Doping: P type iv. Orientation: (100) ± 0.5° v. TTV: ≤ 5 μm vi. Bow and Warp: ≤ 20 μm Growth: CZ [...]

2020-03-25meta-author
What Is PL (Photoluminescence)?

PAM-XIAMEN can supply semiconductor wafers, more wafer specifications please refer to https://www.powerwaywafer.com/products.html. If necessary, we will offer PL (photoluminescence) spectroscopy for the semiconductor wafers. 1. What is PL? About PL, it refers to the self-emission light produced by a material after being excited by light. When [...]

2022-08-09meta-author
Storage Performance Analysis of InSb Compound

Indium antimonide (InSb) compound semiconductor, as a direct bandgap semiconductor material, has low electron effective mass, high mobility, and narrow bandgap width. At low temperatures, InSb compound has a high absorption coefficient for infrared light, with a quantum efficiency greater than or equal to 80%. [...]

2024-01-19meta-author
Silver(Ag) on Si wafer

PAM XIAMEN offers Silver(Ag) on Si wafer . Silver Film on Silicom Wafer ,Ag: 0.2 microns / ,Si(100) P-type R:1-20 ohm.cm Silver Metallic Film  Film Deposition by DC Sputtering  Silver Thickness: 0.2 microns Film Resistivity: N/A Film Crystallinity:  N/A Roughness, RMS:  4.87 nm and  < [...]

2019-04-29meta-author
Growth of InGaN layers on (1 1 1) silicon substrates by reactive sputtering

Growth of InGaN layers on (1 1 1) silicon substrates by reactive sputtering InGaN films were grown on (1 1 1) silicon substrates by reactive magnetron sputtering. It was demonstrated that the indium composition in the InGaN films can be controlled by varying the ratio of the applied radio-frequency [...]

2014-02-08meta-author