PAM XIAMEN offers 6″ Monocrystalline silicon wafers with insulating oxide
6″ Monocrystalline silicon wafers with insulating oxide
Polishing: one-sided for microelectronics
Thickness: 675 +/- 20 microns
TTV <15 μm,
Warping <35 μm
P type
Orientation <100>
The thickness of the insulating oxide layer is 300 nm
Resistance of the base plate ≥ 10 [...]
2020-04-15meta-author
The application fields of SiC wafers and GaN wafers are mainly divided into electronic power field, radio frequency field, optoelectronic field, and other fields. Among them, electronic power field and radio frequency field are the most important applications, and the advantages of using SiC material are obvious. These two areas have [...]
2021-04-20meta-author
Al2O3 (Sapphire)
PAM XIAMEN offers high-quality Al2O3 (Sapphire) with C-Plane (0001) orientation at different size from 5 x 5mm2 to 4”diameter:
1 square Al2O3 substrate 5x5mm,10x10mm&0.25″x0.25″
Al2O3 Sapphire Wafer, C-plane (0001), 5x5x0.5mm, 1sp – ALC=> PAM
Al2O3 Sapphire Wafer, C-plane (0001), 5x5x0.5mm, 2sp – ALC=> PAM
Al2O3- Sapphire Wafer, [...]
2019-04-16meta-author
PAM XIAMEN offers Silicon Wafer Thickness:275+- 25µm.
Silicon Wafer ,2in Si Wafer,P/Boron <111> ON +-1°,
0.01-0.02 Ohm-cm ,275+- 25µm Thickness,SSP,
PRIME -Si Wafers,Single SidePolished/Etched Back,
Primary Semi Std Flat,
Surface Roughness <1nm
For more information, please visit our website: https://www.powerwaywafer.com,
send us email at [...]
2019-08-22meta-author
PAMDPU-1000-01 is a direct current power supply unit in low ripple, low thermal drift and long- term stability. It can supply power to probe in nuclear detection field and others.
1. High Voltage Power Supply Specification
Input
AC220V/50Hz
Output
HV DC 0~500V/0~1000V; LV DC +12V/2W、-12V/1W
Alternative current
2A
Ripple voltage
10ppm (at rated [...]
2021-11-26meta-author
Silicon wafers can be supplied with specifications as found in: https://www.powerwaywafer.com/silicon-wafer
Silicon is a semiconductor material, and its resistivity is closely related to the doping concentration. Doping is that introducing a small amount of impurities into silicon crystals to alter their electrical properties. According to the [...]
2024-03-29meta-author