PAM XIAMEN offers NaCl single crystal substrates.
NaCl single crystal substrates is ideal for growing expitaxial film and studying interface diffusion and defects. The film is easily removed from NaCl substrate by floating it off on water or by dissolving away the underlying substrate. We uses special technique to make supersmooth polishing in 1 mm thick substrate and achieve high quality expitaxial film in a larger area. NaCl is very sensitive to moisture, and must be stored in desiccator box.
| Xtl Structure | Lattice (A) | Melting Point | Density | Growth Method | Max. Xtl Size | Caution |
| Cubic | 5.640 | 801 oC | 2.16 g/cm3 | Solution | 120d x100 | dissove in water |
NaCl (100) +/-3 degree 10x10x2.0mm, 2SP
NaCl (100) +/-3 degree 10x10x2.0mm, 1SP
NaCl (100) +/-3 degree 10x10x2.5 mm, 1SP
NaCl (110) +/-3 degree 10x10x2.0 mm, 1SP
NaCl (111) +/-3 degree 10x10x2.0 mm, 1SP
NaCl single crystal (PAMP16112-NACL) can be also offered:
Diameter: 15 mm;
Length: 15 mm;
Orientation: Flat planes parallel to (100) direction;
Purity: 5N;
One surface polished.
For more information, please contact us email at victorchan@powerwaywafer.com and powerwaymaterial@gmail.com.
Found in 1990, Xiamen Powerway Advanced Material Co., Ltd (PAM-XIAMEN) is a leading manufacturer of semiconductor material in China. PAM-XIAMEN develops advanced crystal growth and epitaxy technologies, manufacturing processes, engineered substrates and semiconductor devices. PAM-XIAMEN’s technologies enable higher performance and lower cost manufacturing of semiconductor wafer.
You can get our free technology service from enquiry to after service based on our 25+ experiences in semiconductor line.