ITO coated(sodalime) glass

PAM XIAMEN offers ITO coated(sodalime) glass.

ITO  Physical properties
Melting point 1800–2200 K (1526-1926 °C) (2800–3500 °F)
Density 7120–7160 kg/m3 at 293 K
Color (in powder form) Pale yellow to greenish yellow, depending on SnO2 concentration
Values vary with composition. SI units and STP are used except where noted.

 

ITO Coated Glass, 10mmx10mmx 0.7mm

ITO Coated Glass Substrate 10mm x 10 mm x 0.7 mm, R:9-15 ohm/sq,Nominal ITO film thickness: 180 nm

ITO Coated Glass, 1″ x1″

ITO Coated Glass Substrate 1″ x 1″ x 0.7 mm, R: 16-19 ohm/sq, Nominal ITO film thickness: 90 nm+/10nm
ITO Coated Glass Substrate 1″ x 1″ x 0.7 mm, R:12-15 ohm/sq, Nominal ITO film thickness: 115 (+/10%) nm
ITO Coated Glass Substrate 1″ x 1″ x 0.7 mm, R:6-7 ohm/sq, Nominal ITO film thickness: 250 nm+/25nm
ITO Coated Glass Substrate 1″ x 1″ x 0.7 mm, R:7-10 ohm/sq, Nominal ITO film thickness: 180 nm
ITO Coated Glass Substrate 1″ x 1″ x 0.7 mm, R:8-10 ohm/sq, Nominal ITO film thickness: 180 nm
ITO Coated Glass Substrate 1″ x 1″ x 1.1 mm, R:8-10 ohm/sq, Nominal ITO film thickness: 180 nm
ITO/ZnO Coated Glass Substrate 1″ x 1″ x 0.7 mm, ITO Film=100nm, ZnO film=50nm

ITO Coated Glass, 1″ x3″x 0.7mm

ITO Coated Glass Substrate 1.0″ x 3″ x 0.7 mm,R: 6-7 ohm/sq, Nominal ITO film thickness: 250 nm+/-25nm
ITO Coated Glass Substrate 1.0″ x 3″ x 0.7 mm,R: 9-12 ohm/sq, Nominal ITO film thickness: 180 nm
ITO Coated Glass Substrate 1.0″ x 3″ x 1.1 mm,R: 100 ohm/sq, Nominal ITO film thickness: 30-35nm, 10 pcs/pack

ITO Coated Glass, 100mm x100mm x 0.7mm

ITO Coated (250 nm) Glass Substrate: 100mm x 100 mm x 0.7 mm, R<7 ohm/sq – ITO-10010007-7K
ITO Coated Glass Substrate with ITO film 115+/-10 nm 100mm x 100 mm x 0.7 mm, 12-15 ohm/sq
ITO Coated Glass Substrate with ITO film 180+/-25 nm 100mm x 100 mm x 0.7 mm, 8-10 ohm/sq
ITO Coated Glass Substrate with ITO film thickness about 90+/-10nm 100mm x 100 mm x 0.7 mm, 16-19ohm/sq
ITO (180nm) Coated Glass Substrate 100x100x0.7 mm, R: 9-15 ohm/sq, – ITO-10010007-15C

ITO Coated Glass,2″x 0.7mm

ITO Coated Glass Substrate 2″ x 0.7 mm, R:9-15 ohm/sq- 1sp,Nominal ITO film thickness: 180 nm

ITO Coated Plastic Film

ITO Coated PEN Plastic Film, 0.125mm Thick x 72mm W x 105mm L, 12 ohm/sq, PEN layer=0.125 mm, ITO layer>180 nm
ITO Coated Plastic PET Film, 0.175mm Thick x 300mm W x 1 M ,R<=14 ohm/sq, ITO layer: 115nm
ITO Coated Plastic PET Film, 0.175mm Thick x 300mm Width x 300mm Length ,14 ohm/sq, ITO layer: 115nm+/- 10nm
ITO Coated Plastic PET Film, 0.175mm Thick x 300mm Width x 5 Meter Length ,14 ohm/sq, ITO layer: 115nm+/- 10nm
ITO Coated Plastic PET Film, 0.175mm Thick x 350mm Width x 1 Meter Length ,60 ohm/sq
ITO Coated Plastic PET Film, 0.175mm Thick x 350mm Width x 300 mm Length ,60 ohm/sq-1
ITO Coated PEN Plastic Film, 0.125 Tx210Wx297L (mm) ,12 ohm/sq , ITO layer>180 nm
PET Film with Single Side Peal-able Silicon Coating (200 mm width x 100um thick, 100 meter/roll)

ITO Film on Corning 7980

ITO film on Corning 7980 ,10x10x 0.5mm R: 9-15 ohm/sq
ITO film ( 180 nm ) on Corning 7980 , 6 “x 6″x 0.5mm R: 9-15 ohm/sq
ITO film ( 180 nm) on Corning 7980 , 1 “x 1″x 0.5mm R: 9-15 ohm/sq

For more information, please visit our website: https://www.powerwaywafer.com,
send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com

Found in 1990, Xiamen Powerway Advanced Material Co., Ltd (PAM-XIAMEN) is a leading manufacturer of semiconductor material in China. PAM-XIAMEN develops advanced crystal growth and epitaxy technologies, manufacturing processes, engineered substrates and semiconductor devices. PAM-XIAMEN’s technologies enable higher performance and lower cost manufacturing of semiconductor wafer.

Our goal is to meet all of your requirements, no matter how small orders and how difficult questions they may be,
to maintain sustained and profitable growth for every customer through our qualified products and satisfying service.

Share this post