CdSe single crystal

CdSe single crystal

PAM XIAMEN offers CdSe single crystal.

CdSe single crystal substrate, (0001) 10x10x1.0mm, 2sp Low Resistivity
CdSe single crystal
Orientation: (0001)
Type:  N
Sizes: 10 x 10 +/- 0.1 mm
Thickness: 1.0 +/- 0.1 mm
Resistivities: < 1 ohm-cm
Surface Quality: two sides optical polished 60/40

CdSe single crystal substrate, (0001) 10x10x1.0mm, 2sp High Resistivity
CdSe single crystal
Orientation: (0001)
Sizes: 10 x 10 +/- 0.1 mm
Thickness: 1.0 +/- 0.1 mm
Resistivities: >E6 ohm-cm
Surface Quality: two sides optical polished 60/40

CdSe single crystal substrate, (10-10) 10x10x1.0mm,2sp Low Resistivity
CdSe single crystal
Orientation (10-10)
Type: N
Sizes: 10 x 10 +/- 0.1 mm
Thickness: 1.0 +/- 0.1 mm
Resistivities: < 1 ohm-cm
Surface Quality: two sides optical polished 60/40

CdSe single crystal substrate, (10-10) 10x10x1.0mm,2sp High Resistivity
CdSe single crystal
Orientation: (10-10)
Sizes: 10 x 10 +/- 0.1 mm
Thickness: 1.0 +/- 0.1 mm
Resistivities: >10^10 ohm-cm
Surface Quality: two sides optical polished 60/40

For more information, please visit our website: https://www.powerwaywafer.com,
send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com

Found in 1990, Xiamen Powerway Advanced Material Co., Ltd (PAM-XIAMEN) is a leading manufacturer of semiconductor material in China. PAM-XIAMEN develops advanced crystal growth and epitaxy technologies, manufacturing processes, engineered substrates and semiconductor devices. PAM-XIAMEN’s technologies enable higher performance and lower cost manufacturing of semiconductor wafer.

With more than 25+years experiences in compound semiconductor material field and export business, our team can assure you that we can understand your requirements and deal with your project professionally.

2019-04-19

Share this post

Related Posts

6″ Silicon Wafer-1

PAM XIAMEN offers 6″ Silicon Wafer. Material Orient. Diam. Thck (μm) Surf. Resistivity Ωcm Comment p-type Si:B [100] 6″ 350 P/P FZ 2,700-3,250 SEMI Prime, 1Flat (57.5mm) p-type Si:B [100] 6″ 900 C/C FZ >50 SEMI Prime, 1Flat, MCC Lifetime>6,000μs n-type Si:P [100] 6″ 825 C/C FZ 7,000-8,000 {7,025-7,856} SEMI, 1Flat, Lifetime=7,562μs n-type Si:P [100-6° towards[111]] ±0.5° 6″ 675 P/P FZ >3,500 SEMI Prime, 1Flat (57.5mm) n-type Si:P [100-6° towards[111]] ±0.5° 6″ 790 ±10 C/C FZ >3,500 SEMI, 1Flat n-type Si:P [100-6° towards[111]] ±0.5° 6″ 675 P/P FZ >1,000 SEMI Prime, Notch on <010> {not on <011>}, Laser Mark n-type Si:P [100-6° towards[111]] ±0.5° 6″ 675 BROKEN FZ >1,000 SEMI notch Test, Broken into many large pieces. One piece [...]

2019-03-04meta-author
Sapphire Substrate Market in 2013

Sapphire Substrate Market in 2013   Will cell phone windows come to the rescue? Significant overcapacity and low LED substrate prices will affect the profitability and viability of many sapphire players in 2013 and beyond, but emerging applications could transform the industry. The sapphire material shortage experienced from [...]

2013-01-10meta-author
Ceramic ALN SUBSTRATE-1

PAM XIAMEN offers Ceramic ALN SUBSTRATE. 100X100 Thickness 0.5±0.03mm Item Unit Value Test Standard 1）Colour —- Gray 3.2 2）Density g/cm³ ≥3.33 GB/T 2413 3）Thermal Conductivity 20℃，W/(m·K) ≥170 GB/T 5598 4）Dielectric Constant 1MHz 8~10 GB/T 5594.4 5）Dielectric Strength KV/mm ≥17 GB/T 5593 6）Flexural Strength MPa ≥450 GB/T 5593 7）Camber Length‰ ≤2‰ 　 8）Surface roughness Ra μm 0.3~0.6 GB/T 6062 9）Water absorption % 0 GB/T 3299-1996 10)Volume resistivity 20℃，Ω.cm ≥1013 GB/T 5594.5 11）Thermal expansivity 10-6/℃ 20~300℃ 2~3 GB/T5593 300~800℃ 2.5~3.5   For more information, please visit our website: https://www.powerwaywafer.com, send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com Found in 1990, Xiamen [...]

2019-07-03meta-author
Electrolytic Removal of P‐Type GaAs Substrates from Thin, N‐Type Semiconductor Layers

An electrolytic etching technique has been developed which can remove p‐type GaAs substrates from thin (2–10µ) n‐type layers of  or . Sodium hydroxide is used as the electrolyte, and is sprayed continually over the etching surface to prevent the build‐up of “flakes” on the p‐type surface [...]

2019-12-23meta-author
SiO2 (single crystal quartz)-2

PAM XIAMEN offers SiO2 (single crystal quartz). Single crystal quartz wafer is an excellent substrate for microwave filters for wireless communication industries. Conversion from the three-index system to the four as [u ‘ v ‘ w ‘ ] —> [u v t w] is [...]

2019-05-15meta-author
How Silicon Carbide (SiC) Chips Are Made?

How is silicon carbide (SiC) chip made? Generally speaking, chips are semi-finished products that have been cut from wafers. PAM-XIAMEN can offer SiC wafers for making chips, more specifications please refer to https://www.powerwaywafer.com/sic-wafer. Each wafer integrates hundreds of chips, and each chip consists of [...]

2022-07-27meta-author