2″CZ Prime Silicon Wafer

2″CZ Prime Silicon Wafer

PAM XIAMEN offers 2″CZ Prime Silicon Wafer

tem1, 100pcs
Silicon wafer:
i. Diameter: 50.8 mm ± 0.5 mm,
ii. Thickness: 275 μm ±25μm,
iii. Doping: P type
iv. Orientation: (100) ± 0.5°
v. TTV: ≤ 5 μm
vi. Bow and Warp: ≤ 20 μm
Growth: CZ
Grade: Prime
Resistivity: 1 Ohm-cm to 10 Ohm-cm
Surface: single side polished
Flats: SEMI Standard
Surface roughness: ≤ 5Å

FAQ 

Q: To study desired magnetic properties of our deposited thin magnetic films sometime we anneal their sample (i.e., substrate + thin film) at high temperatures. Hence this temperature sustainability is required. Hence we require that offered fleaxible Si substrates should withstand 1.6K to 700 K which is (-) 271.5 Degree C to 430 Degree C. Please confirm.

A: The silicon wafers we offered are no problem to withstand 271.5 Degree C to 430 Degree C.

For more information, please contact us email at victorchan@powerwaywafer.com and powerwaymaterial@gmail.com.

2020-03-25

Share this post

Related Posts

Investigation of Te inclusions in CdZnTe crystalline material using Raman spectroscopy and IR techniques

IR images reveal that Te inclusions exist in CdZnTe crystal in the form of square, hexagonal and triangular shapes. The density of Te inclusions for sizes above 5 μm sharply varied from 2.27 × 103 cm−2 to 4.52 × 105 cm−2 with a consequent reduction in IR transmittance from ∼60.5% to ∼55% when the Te-rich volume increased [...]

2013-11-15meta-author , , ,
Fabrication of Ge-on-insulator wafers by Smart-CutTM with thermal management for undamaged donor Ge wafers

Newly engineered substrates consisting of semiconductor-on-insulator are gaining much attention as starting materials for the subsequent transfer of semiconductor nanomembranes via selective etching of the insulating layer. Germanium-on-insulator (GeOI) substrates are critically important because of the versatile applications of Ge nanomembranes (Ge NMs) toward [...]

2019-10-30meta-author
2018 TOP 100 US HIGHER EDUCATION R&D EXPENDITURES

2018 TOP 100 US HIGHER EDUCATION R&D EXPENDITURES post by PAM-XIAMEN  date: Jan 03,2020 University is an important research and development subject in the innovation system. In all 912 US universities, PAM-XIAMEN has compiled the ranking data and the name by source of funds to list top [...]

2020-01-03meta-author
3″ Silicon EPI Wafer-1

PAM XIAMEN offers 3″ Silicon EPI Wafers. Substrate EPI Comment Size Type Res Ωcm Surf. Thick μm Type Res Ωcm 3″Øx381μm p- Si:B[111] 0.004-0.008 P/E 12.5±2.5 p- Si:B 2.35 n/p/p+ 3″Øx381μm p- Si:B[111] 0.004-0.008 P/E 140±10 n- Si:P 33.6 n/p/p+ 3″Øx381μm n- Si:As[111-4°] 0.001-0.005 P/E 5.5 n- Si:P 0.31 – 0.33 n/n+ 3″Øx381μm n- Si:As[111] 0.001-0.005 P/E 37.5 n- Si:P 0.6±10% n/n+ 3″Øx525μm n- Si:P[111] 0.001-0.005 P/E 4.5 n- Si:P 1.1 – 1.4 n/n+, Sealed in cassettes of 24 wafers 3″Øx381μm n- Si:As[111] 0.001-0.005 P/E 5.5 n- Si:P 1.06±10% n/n+ 3″Øx381μm n- Si:As[111] 0.001-0.005 P/E 11 n- Si:P 17.5±10% n/n+ 3″Øx381μm n- Si:As[111] 0.001-0.005 P/E 12 n- Si:P 1.7±10% n/n+ 3″Øx381μm n- Si:As[111] 0.001-0.005 P/E 12 n- Si:P 2.1±10% n/n+ 3″Øx381μm n- Si:As[111] 0.001-0.005 P/E 12 n- Si:P 1.3±10% n/n+ 3″Øx381μm n- Si:As[111] 0.001-0.005 P/E 12 n- Si:P 1.8±10% n/n+ 3″Øx381μm n- Si:As[111] 0.001-0.005 P/E 12 n- Si:P 1.3±10% n/n+ 3″Øx381μm n- Si:As[111] 0.001-0.005 P/E 12 n- Si:P 16±10% n/n+ 3″Øx381μm n- Si:As[111] 0.001-0.005 P/E 13 n- Si:P 1.35±10% n/n+ 3″Øx381μm n- [...]

2019-03-08meta-author
Si-based GaN PIN Photodetector Structure

III-nitrides are suitable for working in extreme conditions due to their excellent radiation hardness and high temperature properties. Therein, the fabrication of various types of GaN-based photodetectors (PDs) has been reported over the past decade. In addition, the high conductivity of silicon substrate has [...]

2022-07-29meta-author
LAALO3 LANTHANUM ALUMINATE CRYSTAL SUBSTRATES

LaAlO3 (Lanthanum Aluminate) substrate is available for. LaAlO3 substrate is commonly used for epitaxial growth of thin films such as high Tc superconductors, magnetic and ferroelectric materials. The dielectric properties of LaAlO3 crystal make it suitable for low loss microwave and dielectric resonance electronics [...]

2019-03-12meta-author