PAM XIAMEN offers 4″ Silicon Wafer.
Material
Orient.
Diam.
Thck
(μm)
Surf.
Resistivity
Ωcm
Comment
n-type Si:As
[111-4°] ±0.5°
4″
325
P/E
0.001-0.005
SEMI Prime, Back Surface: Sand blasted with LTO seal
n-type Si:As
[111-4°] ±0.5°
4″
300
P/E
0.001-0.005
SEMI Prime, Back-side Sand-blasted with LTO seal, in Empak cassettes of 7 wafers
n-type Si:As
[111-2°] ±0.5°
4″
400
P/EOx
0.001-0.004 {0.0018-0.0036}
SEMI Prime, Epi edges, 0.5μm LTO
n-type Si:As
[111-4°] ±0.5°
4″
525
P/E
0.001-0.005
SEMI Prime
n-type Si:As
[111-4°]
4″
525
P/E
0.001-0.005
SEMI Prime
n-type Si:As
[111] ±0.5°
4″
1000
P/E
0.001-0.005 {0.0031-0.0040}
SEMI Prime, TTV<4μm, [...]
2019-03-05meta-author
According to the latest report from LEDinside, a division of the market research firm TrendForce, 2017-2021 LED Industry Demand and Supply Data Base- 2Q17, mainly analyzes top six LED demand and supply market trend in 2017, including IT display market, lighting market trend, automotive LED market [...]
2017-06-05meta-author
Silicon carbide (SiC) is a compound semiconductor material composed of carbon and silicon elements, and is called wide-bandgap semiconductor material because the band gap is greater than 2.2eV. PAM-XIAMEN can provide N-type and semi-insulating SiC wafers. More specifications of SiC wafer please visit https://www.powerwaywafer.com/sic-wafer.
How SiC wafers [...]
2022-08-17meta-author
PAM XIAMEN offers GaAs (100) Te-doped crystal .
GaAs (100), N type Te doped, 10×10 x 0.35 mm, 1SP
GaAs (100), N type Te doped, 5 x 5 x 0.35 mm, 1SP
GaAs (100) orientation, 2 deg OFF Toward [101] +/- 0.5 deg, Te [...]
2019-04-22meta-author
The SOS technology uses single crystal sapphire or spinel insulator material as the substrate and grows a single crystal silicon film through a high-temperature epitaxy process to fabricate semiconductor integrated circuits. It is a kind of SOI CMOS technology. The silicon on sapphire structure [...]
2019-05-16meta-author
Dependence of arsenic antisite defect concentration and two dimensional growth mode on LT GaAs growth conditions
We investigated the dependence of Arsenic antisite defect concentration and that of epitaxial thickness (tepi), above which a transition to three dimensional growth appears, on the growth conditions of [...]