As one of leading SiC epi wafer suppliers, PAM-XIAMEN offers SiC epi wafer, and the SiC epi wafers type includes N type and P type. The SiC epi wafer thickness from 1um to 250um can be produced, and the silicon carbide epi wafer prices are competitive. What is SiC epi wafer? SiC epitaxial wafer is an intermediate link in the core of the SiC industry chain. At present, a whole set of industrial systems from silicon carbide substrates and SiC epi wafers to device preparation have been formed in the world. In the epi wafer market, high-quality SiC epitaxy are the basic materials of SiC power devices. The current development trend of silicon carbide epitaxial materials required by power electronic devices at home and abroad is developing in large diameter, low defects, high uniformity and etc.
1. Технические характеристики 4-дюймовой пластины SiC Epi
Пункт 1:
PAM201221-SIC-EPI
| SiC подложки | |
| Диаметр | 100мм |
| Толщина | 350 мкм |
| Polytype | 4H-SiC, |
| проводимость | N-типа |
| Офф-ориентация | Смещение от оси на 4 градуса |
| MPD | ≤1 / см2 |
| удельное сопротивление | 0,015 ~ 0,028 Ом-см |
| Чистота поверхности | Двусторонняя полировка |
| Слой эпи | |
| Буфер: | |
| Толщина | 0,5 мкм, n-типа |
| Уровень допинга | 1E18см3 |
| Эпи 1: | |
| Толщина | 6 мкм +/- 5% |
| уровень n-допинга | 5.2E15 / см3 |
Пункт 2:
PAM210514-SIC-EPI
| SiC подложки | |
| Диаметр | 100мм |
| Толщина | 350 мкм |
| Polytype | 4H-SiC, |
| проводимость | N-типа |
| Офф-ориентация | Смещение от оси на 4 градуса |
| MPD | ≤1 / см2 |
| удельное сопротивление | 0,015 ~ 0,028 Ом-см |
| Чистота поверхности | Двусторонняя полировка |
| Слой эпи: | |
| Буфер: | |
| Толщина | 0,5 мкм, n-типа |
| Уровень допинга | 1E18см3 |
| Эпи 1: | |
| Толщина | 6 мкм +/- 5% |
| уровень n-допинга | <1E15 / см3 |
| Элементы с низким содержанием O, B, P и Al: | B <0,06 частей на миллион; P <0,05 частей на миллион; Al <0,01 частей на миллион; без O |
2. SiC Epi in the Fields of Low Voltage, Medium Voltage and High voltage
Что касается применения, мы обычно делим карбид кремния на три области: низкое напряжение, среднее напряжение и высокое напряжение. В случае низкого напряжения это в основном для некоторой бытовой электроники, такой как PFC и блоки питания; Среднее напряжение в основном предназначено для автомобильной электроники, а среднее напряжение также является основным направлением применения для разработки SiC epi-пластин в будущем. Третий - это область применения с относительно высокими уровнями напряжения, такая как железнодорожный транспорт и системы электроснабжения выше 3300 В.
В то же время мы видим, что карбид кремния и нитрид галлия по-прежнему конкурируют в области среднего и низкого напряжения, но в области высокого напряжения, с точки зрения зрелости материала, карбид кремния имеет уникальное преимущество. . Однако жаль, что до сих пор не было зрелого продукта в области высокого напряжения. Пластина SiC epi для поля высокого напряжения находится в стадии исследований и разработок во всем мире, но эпитаксиальные пластины из карбида кремния среднего и низкого напряжения уже используются в диодах и продуктах MOSFET на рынке.
3. 100mm 4H SiC Epitaxial Wafer Norm
This norm applies to 4H silicon carbide (4H-SiC) epitaxial wafers. The SiC wafer production is mainly used to manufacture power semiconductor devices or power electronic devices.
3.1 Requirements of 4H-SiC Epitaxial Growth in 4 Inch
The substrate is a (0001) silicon surface 4H-SiC wafer with an angle of 4° in the <11-20> direction. The ratio of 4H crystal type to the total area of the silicon carbide wafer should not be less than 90%. The surface of the wafer can be polished on one side or on both sides. The silicon surface of the wafer should be chemically mechanically polished with a surface roughness of less than 0.5 nm. The number of cleanable particles on the surface of the wafer (diameter ≥0.5 um) does not exceed 15/piece.
3.2 Epitaxial Quality Requirements for the SiC wafer
Surface defects of SiC epitaxy should meet the requirements of the following table.
| Item | Maximum Allowable Limit | |
| Industrial Grade | Research Grade | |
| Carrots | ≤80pcs/wafer | ≤100pcs/wafer |
| Comets | ||
| Triangles | ||
| Downfalls | ||
| Edge Removal | 3 mm | 3 mm |
The surface roughness of SiC wafer in size of 4” should be less than 5.0 nm in the entire 4H-SiC epitaxial wafer range.
The thickness uniformity of the 4-inch SiC epitaxial layer should meet: industrial grade ≤5% and research grade ≤7%
Doping concentration uniformity for industrial grade should be ≤30%, and that for research grade should be ≤35%.
4. FAQ about SiC Epitaxy
Q1: I looked at the SiC homoepitaxial wafers on your company website before, and they all have buffer layer. I would like to ask what is the function of the intermediate buffer layer? What effect will it have on the epitaxial layer if directly epitaxial without a buffer layer?
A: The role of the intermediate buffer layer in SiC homoepitaxy is to reduce defect density and provide epitaxial yield.
Q2: Is there a big difference between the growth temperature of the buffer layer and the epitaxial layer of 4H-SiC epitaxial wafer?
A: There is little difference in growth temperature for buffer and epitaxial layer of 4H-SiC epi wafer.
Q3: I am interested in your standard Instrinsic SiC on 4H SiC substrate.The application is to produce electrochemically suspended membranes of ui doped SiC from a n-type substrate, hopefully of thicknesses between 500nm-2000nm. We are trying to determine the performance of our electrochemical undercut process on Si-face and C-face material. Does high wafer resistivity come from high compensation by deep levels, or from a low concentration of impurities in the epi-layer?
A: If so, I think you need 500nm undoped SiC on n-type SiC substrate. Suggest you use thicker thickness. If you must require 2um, we also can do it, the carrier concentration of undoped SiC should be <1E5, typical ~1E4.
Q4: Is it possible to have 4H-SiC epitaxial on 3C-SiC with 20-40micron thickness?
A: 4H-N SiC on 3C-N SiC is prone to phase transition and is not easy to control. Generally speaking, under epitaxial conditions, it is easier to form 3C crystal forms, so it is difficult to estimate the difficulty of epitaxial 4H on 3C. But we can supply 350um thick freestanding 3C-SiC substrate, more specifications please refer to https://www.powerwaywafer.com/3c-sic-wafer.html.
Для получения дополнительной информации о пластине SiC epi, пожалуйста, обратитесь к:
150 мм 4H п-типа карбида кремния EPI Вафли
Эпитаксиальные пластинки из 4H SiC
Зачем нам нужна эпитаксиальная пластина из карбида кремния?
Для получения дополнительной информации, пожалуйста, свяжитесь с нами по электронной почте по адресу victorchan@powerwaywafer.com и powerwaymaterial@gmail.com.