PAM XIAMEN offers 4″CZ Prime Silicon wafer-16
4″ CZ Silicon Wafer SSP
Silicon wafers, per SEMI Prime,
P/E 4″Ø×525±25μm, SEMI Flats (two),
p-type Si:B[100]±0.5°, Ro=(0.001-0.002)Ohmcm,
One-side-polished, back-side Alkaline etched,
TTV<5μm, Bow/Warp<30μm,
Wafers free of striation marks,
Sealed in Empak or equivalent cassette.
For more information, send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com
2021-01-06meta-author
As reported by Esia(European Semiconductor Industry Association), in January worldwide sales of semiconductors amounted to US$ 26.880 billion. These results are in line with seasonal patterns – as the first months of the year are usually slower for semiconductors – and represent a 2.7% [...]
2016-04-18meta-author
Ge substrates are recently being reconsidered as a candidate material for the replacement of Si substrates in advanced semiconductor devices. The reintroduction of this material requires reengineering of the standard IC processing steps. In this paper, we present the extension of the methodology of [...]
PAM XIAMEN offers high-quality Bi2Te3 single crystal.
Bismuth telluride (Bi2Te3) is a gray powder that is a compound of bismuth and tellurium also known as bismuth(III) telluride. It is a semiconductor which, when alloyed with antimony or selenium is an efficient thermoelectric material for [...]
2019-04-17meta-author
PAM XIAMEN offers 2″ Silicon Oxide Wafer
2″ Silicon Oxide Wafer
Diameter (mm): 50mm
Grade: Prime
Growth: CZ
Type/Dopant: any
Orientation: 100
Resistivity (Ohm-cm): any
Thickness (µm): 500±25μm
Tolerance (µm): any
Surface Finish: SSP
Flats: SEMI-Std.
TTV < (µm): any
Bow < (µm): any
Warp < [...]
2020-04-24meta-author
PAM XIAMEN offers 80+1mm FZ Si Ingot-1
FZ Si Ingot
Diameter 80+1mm, N-type, <111>±2°
Resistivity>3000Ωcm
Oxygen/Carbon Content 10Е16см-3
The silicon content not less than 99.999999%
Length 150-480mm
MCC lifetime>1000μs
The dislocation density not, Swirl not
For more information, send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com
2020-03-13meta-author