Xiamen Powerway offers InSb (indium antimonide) epi wafer with homogeneous structure, which can be used to detect infrared radiation with a wavelength of 8~12um. Homoepitaxial InSb epi wafer on InSb substrate can improve the operating temperature of indium antimonide detector.
InSb epi ready wafer
1. InSb Homogeneous Structures
1.1 [...]
2020-03-25meta-author
PAM XIAMEN offers 4″CZ Prime Silicon Wafer Thickness 525 ± 25 µm.
PRIME WAFERS SILICIUM CZ
DIAMETER 4 inch (100mm+/-0.5mm)
ORIENTATION <1-0-0> +/-1°
THICKNESS : 525µm +/-25µm
SSP
TTV < 10µm – BOW < 40µm
FLAT : 32.5mm
TYPE P
RESISTIVITY : 8 – [...]
2019-07-05meta-author
PAM-XIAMEN can offer 850nm and 940nm infrared LED wafer by MOCVD. 850nm and 940nm infrared LED refers to the infrared wavelength with the peak value of 850nm or 940nm, but there is also a small amount of light in the visible light area, so it [...]
2020-05-14meta-author
PAM XIAMEN offers Silver Single Crystal & Substrate.
PAM XIAMEN grows Silver single crystal along <111> direction up to 20 mm diameter by Modified Bridgeman method. The silver single crystal substrate is cut from the Ag ingot and polished to 30A surface roughness.
PAM [...]
2019-05-08meta-author
Undoped InP Wafer
PAM-XIAMEN offer low doped InP wafer substrate, see the following:
InP wafer,2” (PAM-190507-INP)
Diameter – 50.8±0.5 mm;
Thickness – 350±25 µm;
N type, low doped
Dopant – low doped
Orientation – (100)±0.5°
Flat orientation – SEMI-E/J;
Major flat orientation – (0-1-1) ±0.5°
Major flat length – 16.0±1.0 mm;
[...]
2020-03-18meta-author
PAM-XIAMEN offers GaN on SiC HEMT epitaxial wafer, which is HEMT stacks grown on semi insulation SiC for fabricating microwave RF devices, working on III-N material-growth and devices.
1. GaN on SiC HEMT Wafer for RF Application
No.1 GaN-on-SiC HEMT Epistructure
Wafer size
2”, 3”, 4”, 6”
AlGaN/GaN HEMT structure
Refer 1.2
Carrier density
6E12~2E13 cm2
Hall mobility
1300~2200 [...]
2019-05-17meta-author