Q:The ideal waverlength for us is 465 nm, can you offer?.
A:It is no problem, but you should know the wavelength should be a range, what we will offer you 465+/-2nm.
Q:The ideal waverlength for us is 465 nm, can you offer?.
A:It is no problem, but you should know the wavelength should be a range, what we will offer you 465+/-2nm.
Q:As to the wafer dicing – is it possible to get a non-rectangular dicing? such as 6mm x 8mm size? A:No problem, any size is workable.
Q: For blue wafer epi on flat substrate, it would be important to omit / leave out the u-GaN layer as we want to LLO and backside conacting. Is that possible? A:Yes, it is no problem, some clients bought our wafers for LLO.
Q: I am not sure whether practically LLO can be done on the PSS given it is not a flat surface A: “laser lift-off” actually is according to “NL layer” as below image. If the NL layer is GaN layer, when it is heating to constant high [...]
Q:For 4” pss wafer, the light comes out from the p-GaN side not from sapphire, so I can’t do flip chip packaging. Also I don’t know whether laser liftoff is possible for pss wafer. Is it possible you can share any image of the etched surface of [...]
Q: What is the highest temperature and the highest thermal shock that the wafers can withstand? A: At the temperatures higher than 1000 C on the free surface of Si-face of 6H-SiC (0001) the carbon segregation properties are started so that during short time the thin [...]
Q:What atomic ratio for Si/C in SiC ? A:Atomic ratio for Si/C in SiC is 1:1