YVO4 UNDOPED YTTRIUM ORTHOVANADATE CRYSTAL

PAM XIAMEN offers YVO4 Undoped Yttrium Orthovanadate Crystals.

UNDOPED YVO4 IS AN EXCELLENT NEWLY DEVELOPED BIREFRINGENCE OPTICAL CRYSTAL.
It has very good transmission in a wide wavelength range from visible to infrared.
It has large index of refractivity and birefringence difference.
Compared with other important birefringence crystals, YVO4 has higher. hardness, better fabrication property, water insoluble and man-made than calcite (CaCO3 single crystal).
Easier to get large, high quality crystal and lower cost than rutile (TiO2 single crystal).

SPECIFICATIONS
Crystal structure: Cubic
Crystal orientation: <111>
Lattice Parameter:  a=12.01Å
Density: 4.56（g/cm3）
Hardness: 8.5（mohs）
Melt point: 1970℃
Thermal expansion: 7.8 x 10-6 /℃
Size available（mm）: 25×25×0.5mm、10×10×0.5mm、10×5×0.5mm、5×5×0.5mm
Special size and orientation are available upon request
Surface roughness(Ra): <=5 Å
Polishing: Single or double
Packing: Clean room

For more information, please visit our website: https://www.powerwaywafer.com,
send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com

Found in 1990, Xiamen Powerway Advanced Material Co., Ltd (PAM-XIAMEN) is a leading manufacturer of semiconductor material in China. PAM-XIAMEN develops advanced crystal growth and epitaxy technologies, manufacturing processes, engineered substrates and semiconductor devices. PAM-XIAMEN’s technologies enable higher performance and lower cost manufacturing of semiconductor wafer.

You can get our free technology service from enquiry to after service based on our 25+ experiences in semiconductor line.

2019-03-18

Share this post

Related Posts

Structural and compositional characterization of MOVPE GaN thin films transferred from sapphire to glass substrates using chemical lift-off and room temperature direct wafer bonding and GaN wafer scale MOVPE growth on ZnO-buffered sapphire

GaN thin films were grown on ZnO/c-Al2O3 with excellent uniformity over 2 in. diameter wafers using a low temperature/pressure MOVPE process with N2 as a carrier and dimethylhydrazine as an N source. 5 mm×5 mm sections of similar GaN layers were direct-fusion-bonded onto soda lime glass substrates [...]

2013-09-11meta-author
Hybrid Chips of Gallium Nitride and Silicon

Hybrid Chips of Gallium Nitride and Silicon Researchers at MIT say they’ve made a big step toward combining the capabilities of the silicon used in computer chips with properties of the compound semiconductors found in lasers and high-powered electronics. In the October issue of IEEE Electron [...]

2014-08-11meta-author , , ,
LD Bare Bar for 808nm@cavity 2mm

PAM XIAMEN offers LD Bare Bar for 808nm@cavity 2mm. Brand: PAM-XIAMEN Wavelength: 808nm Filling Factor: 38% Output Power: 100W Cavity Length:2mm For more information, please visit our website: https://www.powerwaywafer.com, send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com Found in 1990, Xiamen Powerway Advanced Material Co., [...]

2019-05-09meta-author
GaAs (100) crystal-5

P type GaAs(Gallium Arsenide) Wafer PAM XIAMEN offers p type GaAs(100) Zn-doped crystal Wafer. 1.Wafer List: GF-GaAs (100) orientation, Zn-doped 10x10x0.625 mm, single side polished. GaAs Wafer – Growing Method: VGF (100) Zn doped P-type, , 2″x0.5 mm, single side polished, (1-5) x 10^19 /cm^3 [...]

2019-04-22meta-author
Origin, modeling and suppression of grinding marks in ultra precision grinding of silicon wafers

A phenomenon commonly encountered in grinding of silicon wafers is the grinding marks, which are difficult to remove by subsequent polishing process, and have been a great obstacle to the manufacture of silicon wafers with higher flatness. In this paper, the grinding marks formation [...]

2013-09-13meta-author
10*10 mm2 N-GaN Freestanding GaN Substrate

PAM-XIAMEN, one of leading GaN substrate manufacturers, offers 10*10mm2 N-Type Freestanding GaN Substrate. To get more specific information please see the table below: 1. N-Type Freestanding GaN Substrate Specification Item PAM-FS-GAN-50-N Dimension 10 x 10.5 mm2 Thickness 380+/-50um Orientation C plane (0001) off angle toward M-axis 0.35 ±0.15° Conduction Type N-type / Si Doped Resistivity (300K) < 0.05 Ω·cm TTV ≤ 10 µm BOW BOW ≤ 10 µm Surface Roughness: Front side: Ra<0.2nm, epi-ready; Back side: Fine Ground or polished. Dislocation Density ≤5x 106 cm-2 (calculated by CL)* Macro Defect Density 0 cm-2 Useable Area > 90% (edge exclusion)   Package each in single wafer container, under nitrogen atmosphere, packed in [...]

2020-08-17meta-author