PAM-PL01 series detectors are linear pixel electrode structured detector based on CZT crystal, they can counting X-ray and imaging.
1. Specification of CZT Photon Counting Linear Array Detector
Size
16 pixels
Detector crystal
CdZnTe
Crystal Density
5.8g/cm3
Volume resistivity
>1010Ω.cm
Dimension
16.5×4.4 mm2
Thickness
2.0 mm
Pixel array
16×1
Pixel size
0.9×2.0mm2
Electrode material
Au
Standard working voltage
-450V
Max. working voltage
600V
Single pixel leakage current
<0.1nA
Max. counting rate
>0.7Mcps/mm2
Operation temperature
25℃~35℃
Storage temperture
10℃~40℃
Storage [...]
2019-04-24메타 작성자
PAM XIAMEN offers 2″ Diameter Wafer-2″ wafers(111).
2″ Diameter Wafer
2″ wafers(111)
Ge <111> undoped
Ge Wafer . Undoped, 2″ dia x 0.5 mm, 1SP (111) R >50 ohm.cm
Ge Wafer . Undoped, 2″ dia x 0.5 mm, 2SP (111) R >50 Ohm.cm
Ge<111> [...]
2019-04-23메타 작성자
PAM XIAMEN offers MgAl2O4 Magnesium Aluminate Crystal substrate.
Magnesium aluminate (spinel) single crystals are widely used in ultrasonic and microwave material and device related epitaxial growth. We also offer polycrystalline spinel optical windows.
Crystal Structure: Cubic
Lattice parameter: a = 8.085 A
Melting point (℃): 2130℃
Density: 3.64 g/cm3
Hardness: 8 Mohs
Available orientations: <100>, <111>, <110> [...]
2019-03-14메타 작성자
PAM-XIAMEN offers (20-2-1) Plane U-GaN Freestanding GaN Substrate
Item
PAM-FS-GAN(20-2-1)-U
Dimension
5 x 10 mm2 or 5 x 20 mm2
Thickness
380+/-50um
Orientation
(20-21)/(20-2-1) plane off angle toward A-axis 0 ±0.5°
(20-21)/(20-2-1) plane off angle toward C-axis -1 ±0.2°
Conduction Type
N-type / Undoped
Resistivity (300K)
< 0.1 Ω·cm
TTV
≤ 10 µm
BOW
BOW ≤ 10 µm
Surface Roughness:
Front side: Ra<0.2nm, epi-ready;
Back side: Fine Ground or polished.
Dislocation Density
≤5 x 106 cm-2
Macro Defect Density
0 cm-2
Useable Area
> 90% (edge exclusion)
Package
each in single wafer container, under nitrogen atmosphere, packed in class 100 clean room
For more information, please contact us email at victorchan@powerwaywafer.com and powerwaymaterial@gmail.com
2020-09-02메타 작성자
The behaviour of n-6H SiC in HF- and KOH-based electrolytes is studied. It is shown that at the room temperature the dissolution of SiC in these electrolytes is accompanied by a number of side effects, such as passivation of the etched surface with an [...]
2019-03-25메타 작성자
PAM XIAMEN offers 4″ FZ Intrinsic Si wafer
SEMI-PRIME, FZ, 4″, Intrinsic/Undoped, <1-0-0>, >10,000 ohm-cm, 500±15um, SSP, TTV<5um, Bow<30um, Warp <30um,
Flats: 1 Flat.
Particle @0.3µm, <20count
For more information, send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com