PAM XIAMEN offers Magnesium Fluoride MgF2 Crystal.
Magnesium fluoride, MgF2, crystals have been widely used as windows, lenses, and prisms for wavelength from 110 nm to 7.5 um. It is the most suitable material for ArF excimer lasers used in pulsed laser deposition techniques. For its excellent ulta-violet transmittance at 193nm, it is effective as optical polarizing element.
PAM XIAMEN offers the following choices:
Customized crystal growth and machining
High quality MgF2 blank crystal materials in discs, plates, rods, customized for customers
High quality MgF2 VUV windows for ArF Excimer Laser
Customized MgF2 optics for IR and VUV applications
MgF2 viewport windows for Infrared thermography from 8 um to 14 um.
Capability:
maximum diameter: 170 mm, can custom to 10 x 10 mm, 20 x 20 mm, 30 x30 mm, 40x40m
Clear aperture: 85%
Surface flatness: λ/4 at 633 nm
Surface quality: 20/10
Optical Properties | |
Transmission Range | 110 nm to 7.5 μm |
Transmittance | >90% at 193 nm to 6 μm |
Refractive Index | No=1.37608; Ne=1.38771 (at 0.7μm) |
Reflection Loss | 5.2% at 0.6 μm (both surfaces) |
Residual Radiation Peak | 20 nm |
Absorption Coefficient | 0.04 cm-1 at 2.7 μm |
dn/dT | 2.3 x 10-6 /℃ parallel c-axis |
1.7 x 10-6 /℃ perpendicular c-axis | |
Physical Properties | |
Density | 3.18 g/cm3 |
Melting Point | 1255℃ |
Thermal Conductivity | 0.3 Wm-1K-1 at 300K |
Thermal Expansion | 13.7 x 10-6 /℃ parallel c-axis |
8.9 x 10-6 /℃ perpendicular c-axis | |
Knoop Hardness | 415 with 100g indenter (kg/mm2) |
Specific Heat Capacity | 1003 J/(kg.k) |
Dielectric Constant | 1.87 at 1MHz parallel c-axis |
1.45 at 1MHz perpendicular c-axis | |
Youngs Modulus (E) | 138.5 GPa |
Shear Modulus (G) | 54.66 GPa |
Bulk Modulus (K) | 101.32 GPa |
Elastic Coefficient | C11=164; C12=53; C44=33.7 |
C13=63; C66=96 | |
Apparent Elastic Limit | 49.6 MPa (7200 psi) |
Poisson Ratio | 0.276 |
Chemical Properties | |
Solubility | 0.0002 g/ 100g water at 20℃ |
Molecular Weight | 62.32 |
Structure | Tetragonal Crystal |
Cleavage Plane | -110 |
For more information, please visit our website: https://www.powerwaywafer.com,
send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com
Found in 1990, Xiamen Powerway Advanced Material Co., Ltd (PAM-XIAMEN) is a leading manufacturer of semiconductor material in China.PAM-XIAMEN develops advanced crystal growth and epitaxy technologies, manufacturing processes, engineered substrates and semiconductor devices.PAM-XIAMEN’s technologies enable higher performance and lower cost manufacturing of semiconductor wafer.
You can get our free technology service from enquiry to after service based on our 25+ experiences in semiconductor line.