We are an expert of semiconductor wafers in semiconductor industry, and we offer technology support and wafers selling for thousands of univerisities and industrial customers by our decades experience, including Cornell University, Stanford Univeristy,Peking University, Shandong Univerity, university of south carolina,Caltech Faraon lab (USA),University of California, Irvine (USA),Singapore MIT Alliance for Research and Technology Centre (SMART),West Virginia University,Purdue Univerity, University of California, Los Angeles,King Abdullah University of Science & Technology,Massachusetts Institute of Technology,University of Houston,University of Wisconsin,University of Science and Technology of China etc.
And now we show one article example as follows, who bought our wafers or service:
Article title:Evidence for Deep Acceptor Centers in Plant Photosystem I Crystals
Published by:
Irina Volotsenko ; Michel Molotskii ; Anna Borovikova ; Nathan [...]
2019-12-09meta-author
PAM XIAMEN offers Multilayer Graphene on Nickel foil: 2″”x2″” and Pyrolytic Graphite Substrate & Foam.
Isomolded Graphite Plate, Fine Ground, 0.125″T x 4″W x 4″L for Fuel Cell
Pyrolytic Graphite Substrate, C axis Textured, 10x10X0.5 mm, One Side Polished
Pyrolytic Graphite Substrate, C axis Textures, 1″W x [...]
2019-05-06meta-author
HEMTs evolved from Field Effect Transistors (FETs) are suitable for manufacturing monolithic microwave integrated circuits (MMICs).
HEMTs were initially generated to obtain high electron mobility in semiconductor devices at room temperature. The electron mobility of FETs is limited even with high doping levels, so high [...]
2022-07-25meta-author
PAM XIAMEN offers PMN-PT Crystals.
10 x 10 x 0.5 mm PMN-PT Piezoelectric Crystal (111) Pb(Mg1/3Nb2/3)O3-PbTiO3 SSP
10 x 10 x 0.5 mm Pyroelectric Crystal PMN-PT (111) Pb(Mg1/3Nb2/3)O3-PbTiO3 SSP
5 x 10 x 0.5 mm PMNT Electro-Optic Crystal (001) Pack SSP
5 x 10 x 0.5 mm PMNT [...]
2019-03-14meta-author
PAM-XIAMEN offers (10-11) Plane U-GaN Freestanding GaN Substrate
Item
PAM-FS-GAN(10-11)-U
Dimension
5 x 10 mm2 or 5 x 20 mm2
Thickness
380+/-50um
Orientation
(10-11) plane off angle toward A-axis 0 ±0.5°
(10-11) plane off angle toward C-axis -1 ±0.2°
Conduction Type
N-type / Undoped
Resistivity (300K)
< 0.1 Ω·cm
TTV
≤ 10 µm
BOW
BOW ≤ 10 µm
Surface Roughness
Front side: Ra<0.2nm, epi-ready;
Back side: Fine Ground or polished.
Dislocation Density
≤ 5 x 10 6cm-2
Macro Defect Density
0 cm-2
Useable Area
> 90% (edge exclusion)
Package
each in single wafer container, under nitrogen atmosphere, packed in class 100 clean room
For more information, please contact us email at victorchan@powerwaywafer.com and powerwaymaterial@gmail.com