PAM XIAMEN offers test grade silicon wafers
Below is just a short list of the test grade silicon substrates!
Inches | Cust class | Dopant | Type | Orientation | PFL length | PFL direction | SFL | Off orientation | Resistivity | Diameter | Thickness | Bow | TTV | Warp |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.25 ° | 1.5 ± 0.5 Ohmcm | 150 ± 0.5 mm | 280 ± 2.5 µm | 30 | 1,25 | 30 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,20 | 0.0 ± 0.5° | 1-4 Ohmcm | 150 ± 0.2 mm | 375-425 µm | 40 | 5 | 40 | |
6 | DSP | Phosphorus | N | 100 | 47,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5° | 8 – 24 Ohmcm | 150 ± 0.5 mm | 525 ± 5 µm | 30 | 1 | 30 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.00 ± 0.5° | 1 – 4 Ohmcm | 150 ± 0.2 mm | 400 ± 10 µm | 40 | |||
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,20 | 0.0 ± 0.5° | 1 – 3 Ohmcm | 150.0 ± 0.2 mm | 400 ± 5 µm | 50 | 3 | 50 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,20 | 0.0 ± 0.2° | 1-4 Ohmcm | 150 ± 0.2 mm | 325-375 µm | 40 | 5 | 40 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 1 | 0.0 ± 1.0° | 0.5 – 2.0 Ohmcm | 150 ± 0.2 mm | 400 ± 20 µm | 30 | 2 | 30 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5° | 1 – 25 Ohmcm | 150 ± 0.2 mm | 400 ± 10 µm | 50 | 5 | 50 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 1 | 0.0 ± 1.0° | 10 – 20 Ohmcm | 150 ± 0.2 mm | 450 ± 5 µm | ||||
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 1 | 0.0 ± 1.0° | 10 – 20 Ohmcm | 150 ± 0.2 mm | 450 ± 5 µm | ||||
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5° | 3 – 9 Ohmcm | 150 ± 0.2 mm | 300 ± 10 µm | 50 | 2 | 50 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.25 ° | 1.5 ± 0.5 Ohmcm | 150 ± 0.5 mm | 280 ± 2.5 µm | 30 | 1,25 | 30 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5° | 2 – 7 Ohmcm | 150 ± 0.2 mm | 325 ± 5 µm | 3 | |||
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 1 | 0.0 ± 0.5° | 0.5 – 2.0 Ohmcm | 150 ± 0.2 mm | 400 ± 5 µm | 30 | 2 | 30 | |
6 | DSP | Phosphorus | N | 100 | 47,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5° | 8 – 24 Ohmcm | 150 ± 0.5 mm | 525 ± 5 µm | 30 | 1 | 30 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5° | 3 – 7 Ohmcm | 150 ± 0.2 mm | 625 ± 5 µm | 2 | 60 | ||
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 1 | 180 ± 5.0 °, 20.00 ± 2.50 mm | 0.0 ± 0.5° | 1.4 – 6.0 Ohmcm | 150 ± 0.2 mm | 390 ± 5 µm | 38 | 2 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5° | 3 – 5 Ohmcm | 150 ± 0.5 mm | 390 ± 5 µm | 2 | |||
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,0 | 110 ± 1 | 0.0 ± 1.0 ° | 4 – 7 Ohmcm | 150 mm | 380 ± 1 µm | ||||
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,10 | 0.0 ± 0.1° | 5 – 20 Ohmcm | 150 ± 0.2 mm | 450 ± 15 µm | 2 | 40 | ||
6 | DSP | Phosphorus | N | 100 | 47,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5° | 8 – 24 Ohmcm | 150 ± 0.5 mm | 525 ± 5 µm | 30 | 1 | 30 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,0 | 110 ± 1 | 0.0 ± 0.2° | 4 – 7 Ohmcm | 150 ± 0.2 mm | 600 ± 5 µm | 35 | 3 | 35 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5 ° | 1 – 10 Ohmcm | 150 ± 0.5 mm | 250 ± 4.5 µm | 40 | 2 | ||
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5° | 0.5 – 2.0 Ohmcm | 150 ± 0.2 mm | 300 ± 5 µm | 50 | 1 | 50 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5° | 0.5 – 2.0 Ohmcm | 150 ± 0.2 mm | 300 ± 5 µm | 50 | 1 | 50 | |
6 | DSP | Phosphorus | N | 100 | 47,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5° | 0.5 – 1.0 Ohmcm | 150 ± 0.2 mm | 495 ± 5 µm | 40 | 3 | 40 | |
6 | DSP | Phosphorus | N | 110 | 57,5 ± 2,5 | 110 ± 1 | 0.0 ± 1° | 4 -10 Ohmcm | 150 ± 0.2 mm | 1300 ± 15 µm | ||||
6 | DSP | Phosphorus | N | 100 | 47,5 ± 2,5 | 110 ± 1 | 0.0 ± 1.0° | 1 – 5 Ohmcm | 150 ± 0.15 mm | 550 ± 4 µm | 30 | 2 | 30 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5° | 1 – 4 Ohmcm | 150 ± 0.2 mm | 250 ± 10 µm | 40 | 5 | 40 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,0 | 110 ± 1 | 0.0 ± 0.2° | 4 – 7 Ohmcm | 150 ± 0.2 mm | 600 ± 5 µm | 35 | 3 | 35 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,0 | 110 ± 1 | 0.0 ± 0.2° | 4 – 7 Ohmcm | 150 ± 0.2 mm | 380 ± 5 µm | 35 | 1 | 35 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5° | 0.675 – 1.125 Ohmcm | 150 ± 0.2 mm | 400 ± 5 µm | 3 | |||
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 1 | 0 ± 0.5° | 15 Ohmcm ± 30% | 150 ± 0.5 mm | 675 ± 20 µm | 50 | 7 | 50 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5° | 3 – 7 Ohmcm | 150 ± 0.2 mm | 625 ± 5 µm | ||||
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 1 | 0.0 ± 1.0 ° | 1 – 10 Ohmcm | 150.0 ± 0.2 mm | 600 ± 5 µm | 1 | 60 | ||
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5° | 3 – 7 Ohmcm | 150 ± 0.2 mm | 625 ± 5 µm | 2 | 60 | ||
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,20 | 0.0 ± 0.5° | 1-4 Ohmcm | 150 ± 0.2 mm | 375-425 µm | 20 | 4 | 40 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,30 | 0.0 ± 0.5 ° | 1 – 10 Ohmcm | 150 ± 0.2 mm | 550 ± 5 µm | ||||
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 1.0° | 10 – 20 Ohmcm | 150 ± 0.2 mm | 450 ± 5 µm | 30 | 2 | 30 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,20 | 0.0 ± 0.2° | 4 – 7 Ohmcm | 150 ± 0.2 mm | 380 ± 5 µm | 1 | |||
6 | DSP | Phosphorus | N | 100 | 47,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5° | 8 – 24 Ohmcm | 150 ± 0.5 mm | 525 ± 5 µm | 30 | 1 | 30 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5° | 1 – 10 Ohmcm | 150 ± 0.2 mm | 400 ± 5 µm | 1 | |||
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 1 | 0.0 ± 0.6° | 10.5 – 19.5 Ohmcm | 150 ± 0.2 mm | 675 ± 20 µm | 25 | 4 | 35 | |
6 | DSP | Phosphorus | N | 100 | 57,5 ± 2,5 | 110 ± 1 | 0.0 ± 0.5° | 0.5 – 2.0 Ohmcm | 150 ± 0.5 mm | 400 ± 10 µm | ||||
6 | DSP | Red Phos. | N+ | 100 | 57,5 ± 2,5 | 011 ± 1 | 0.0 ± 0.5 ° | 0.01 – 0.02 Ohmcm | 150.0 ± 0.2 mm | 380 ± 10 µm | 60 | 2 | 60 | |
6 | DSP | Red Phos. | N+ | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.2° | 0.01 – 0.02 Ohmcm | 150 ± 0.2 mm | 300 ± 5 µm | 20 | 2 | 50 | |
6 | DSP | Red Phos. | N+ | 100 | 47,5 ± 2,5 | 110 ± 0,20 | 0.0 ± 0.2° | < 0.0019 Ohmcm | 150 ± 0.5 mm | 400 ± 5 µm | 40 | 1 | 40 | |
6 | DSP | Red Phos. | N+ | 100 | 47,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5 ° | < 0.002 Ohmcm | 150 ± 0.5 mm | 625 ± 5 µm | ||||
6 | DSP | Red Phos. | N+ | 100 | 57,5 ± 2,5 | 110 ± 0,50 | 0.0 ± 0.5° | 0.010 – 0.020 Ohmcm | 150 ± 0.2 mm | 400 ± 5 µm | 60 | 10 | 60 | |
6 | DSP | Red Phos. | N+ | 100 | 47,5 ± 2,5 | 110 ± 0,20 | 0.0 ± 0.2° | < 0.0019 Ohmcm | 150 ± 0.5 mm | 400 ± 5 µm | ||||
6 | SSP | Antimony | N+ | 100 | 47,5 ± 2,5 | 110 ± 2 | 0.0 ± 0.5 ° | 0.007 – 0.020 Ohmcm | 150 ± 0.5mm | 625 ± 25 µm |
For more information, please visit our website: https://www.powerwaywafer.com,
send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com
Found in 1990, Xiamen Powerway Advanced Material Co., Ltd (PAM-XIAMEN) is a leading manufacturer of semiconductor material in China.PAM-XIAMEN develops advanced crystal growth and epitaxy technologies, manufacturing processes, engineered substrates and semiconductor devices.PAM-XIAMEN’s technologies enable higher performance and lower cost manufacturing of semiconductor wafer.
You can get our free technology service from enquiry to after service based on our 25+ experiences in semiconductor line.