PAM XIAMEN offers FZ & MCZ silicon ingot and silicon wafer:
Description
Growth Method
—
MCZ
Single crystal size
inch
2 – 8
Conductivity Type
—
N
P
Doped elements
—
P/Sb
B
Crystal Orientation
—
<111>
<110>
<100>
<111>
<110>
<100>
Resistivity
Ω.cm
0.0015-100
0.001-100
RRG
%
20
20
Oxygen Concentration
atoms/cm3
1.00E+18
1.00E+18
Carbon Concentration
atoms/cm3
5.00E+16
5.00E+16
Diameter
mm
55-157
55-157
Length
mm
50-500
50-500
Dislocation
EA/cm2
N/A
N/A
Swirl(After Oxidation)
—
N/A
N/A
Remarks:The above parameters can be customized.
FAQ about MCZ Silicon Wafers
Q:This is just a curiosity, but let me ask about the production method of [...]
2019-02-27meta-author
PAM XIAMEN offers PET film.
PET Film with protective film ,200mm×300mmx Minimum thickness-200um
PET Film with protective film
Size:,200mm×300mm
Minimum thickness: -200um
For more information, please visit our website: https://www.powerwaywafer.com,
send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com
Found in 1990, Xiamen Powerway Advanced Material [...]
2019-05-14meta-author
SiC wafer can be used to manufacture BJT (bipolar junction transistor) devices with low conduction resistance and high blocking voltage up to tens of kilovolts. For applications with a blocking voltage of 4.5kV and higher, bipolar SiC power devices will have more practical application value than unipolar SiC power [...]
2023-11-28meta-author
PAM XIAMEN offers high-quality Au – Gold Single Crystal & Substrate.
PAM XIAMEN grows Gold single crystal along <111> direction upto 20 mm diameter by Modified bridgman method. The Gold single crystal subsrtae is cut from the Gold ingot and polished to 30A surface [...]
2019-04-16meta-author
PAM XIAMEN offers 4″ Silicon Wafer.
Material
Orient.
Diam.
Thck
(μm)
Surf.
Resistivity
Ωcm
Comment
n-type Si:P
[100]
4″
525
P/P
1-100
SEMI Prime, TTV<5μm
n-type Si:P
[100]
4″
525
P/E
0.3-0.5
SEMI
n-type Si:P
[100]
4″
300
P/E
0.29-0.31
SEMI Prime
n-type Si:P
[100]
4″
200
P/P
0.10-0.15
SEMI Test, Not sealed both sides scratched
n-type Si:P
[100]
4″
200
P/P
0.10-0.15
SEMI Test, Both sides with scratches
n-type Si:P
[100]
4″
200
P/E
0.10-0.15
SEMI Prime, Front-side Prime, Back-side Test grade polish
n-type Si:Sb
[100]
4″
525
P/E
0.020-0.022
Prime
n-type Si:Sb
[100-6° towards[110]] ±0.5°
4″
525
P/E
0.015-0.020
SEMI Prime
n-type Si:Sb
[100]
4″
525
P/E
0.011-0.014
Prime
n-type Si:Sb
[100]
4″
305 ±3
P/P
0.010-0.025
SEMI Prime, TTV<1μm
n-type Si:Sb
[100]
4″
525
P/E
0.01-0.02
SEMI Prime, TTV<5μm
n-type Si:Sb
[100]
4″
525
P/E
0.01-0.02
SEMI Prime
n-type Si:As
[100]
4″
525
P/E
0.0025-0.0035
SEMI Prime
n-type [...]
2019-03-05meta-author
PAM XIAMEN offers 8″ Prime Silicon Wafer.
Silicon wafers, per SEMI Prime,
P/E 8″(200.0±0.2mm) Ø×1,000±25µm,
p-type Si:B[111]±0.5°, Ro: <100 Ohmcm,
TTV<6µm, Bow<60µm, Warp<60µm,
One-side-polished, Particles: ≤10@≥0.3µm,
Back-side etched, SEMI notch,
Sealed in Empak or equivalent cassette.
For more information, please visit our website: https://www.powerwaywafer.com, [...]