Lanthanum aluminate (LaAlO3) single crystal substrate is the large-scale high-temperature superconducting film,which has good match with YBaCuO and other high temperature superconductor materials and lattice, low dielectric constant and small microwave loss, so LaAlO3 substrate is suitable for making high temperature superconductor microwave electronic devices (such as high temperature superconductor microwave filter in remote communication).
1.Specification of LaAlO3 Single Crystal Substrate
Growth Method | CZ |
Crystal Structure | Hexagon(Room Temperature) |
Cube(>435℃) | |
Lattice Constants | Hexagon a=5.357A |
c=13.22 A | |
Cube a=3.821 A | |
Density | 6.52g/cm3 |
Melt Point | 2080℃ |
Hardness | 6.5 Mohs |
Dielectric Constant | 24.5 |
CTE | 9.2×10-6/k |
Tangent Loss(10GHz) | ~3×10-4(300k) ~0.6×10-4(77k) |
Apprearance | The color and appearance vary according to the annealing condition, from brown yellow to brown |
Chemical Stability | insoluble in mineral acid at room temperature, soluble in phosphoric acid (H3PO4) at temperature higher than 150 ℃ |
2.Size List of LaAlO3 Single Crystal Substrate
2-1(100)Orient LaAlO3 Substrates, (001)would be the same.
LaAlO3 (100) orientation. 5 x 5 x 0.5 mm substrates , 2 side Epi polished
LaAlO3, (100) orientation. 5 x 5 x 0.5 mm substrates , 1SP
LaAlO3, (100) orientation. 3×3 x 0.5 mm substrates , 1SP
LaAlO3, (100) orientation 10 x 5 x 0.5 mm substrates , 1 side Epi polished
LaAlO3, (100) orientation. 10 x 5 x 1.0mm substrates , 1 side Epi polished
LaAlO3, (100) orientation. 10x10x1.0 mm substrates , 2 side EPI polished
LaAlO3, (100) orientation. 10x10x1.0 mm substrates, 1 side EPI polished”
LaAlO3,(100) orientation 10x10x 0.5mm substrates , 1 SP
LaAlO3,(100) orientation. 10x10x 0.5mm substratess , 2 side EPI polished
LaAlO3,(100) orientation 15x15x 0.5mm substrates , 1 SP”
LaAlO3, (100) orientation. 1″x 1″ x 0.5mm substrates , 2 side epi polished
LaAlO3,(100) orientation. 1″x 1″ x 0.5mm substrates, 1 side epi polished
LaAlO3, (100) orientation. 20×20 x 0.5mm substrates , 2 side epi polished
LaAlO3, (100) orientation. 20×20 x 0.5mm substrates , one side polished
2-2 (110) or (111) LaAlO3 are also available.
For more information, please send us email at victorchan@powerwaywafer.com