PAM XIAMEN offers Ceramic ALN SUBSTRATE.
100X100 Thickness 1.0±0.03mm
Item
Unit
Value
Test Standard
1)Colour
—-
Gray
3.2
2)Density
g/cm³
≥3.33
GB/T 2413
3)Thermal Conductivity
20℃,W/(m·K)
≥170
GB/T 5598
4)Dielectric Constant
1MHz
8~10
GB/T 5594.4
5)Dielectric Strength
KV/mm
≥17
GB/T 5593
6)Flexural Strength
MPa
≥450
GB/T 5593
7)Camber
Length‰
≤2‰
8)Surface roughness Ra
μm
0.3~0.6
GB/T 6062
9)Water absorption
%
0
GB/T 3299-1996
10)Volume resistivity
20℃,Ω.cm
≥1013
GB/T 5594.5
11)Thermal expansivity
10-6/℃
20~300℃
2~3
GB/T5593
300~800℃
2.5~3.5
For more information, please visit our website: https://www.powerwaywafer.com,
send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com
Found in 1990, Xiamen [...]
2019-07-03meta-author
PAM XIAMEN offers high-quality Au – Gold Single Crystal & Substrate.
PAM XIAMEN grows Gold single crystal along <111> direction upto 20 mm diameter by Modified bridgman method. The Gold single crystal subsrtae is cut from the Gold ingot and polished to 30A surface [...]
2019-04-16meta-author
PAM XIAMEN offers ZnTe single crystal substrate.
ZnTe single crystal substrate, undoped, N type, (110) 10x10x 0.5mm, 2sp
ZnTe Random orientation , n type, 10x10x0.5 mm, 2sp
ZnTe single crystal substrate, undoped, P-type (100) 10x10x1.0mm, single side with scratch/dig 60/40
ZnTe, N type, (110) [...]
2019-05-21meta-author
GaN Substrates Offer High Performance At A Price
GaN substrates are manufactured by only a handful of companies at prices prohibitive to volume production, but offer great potential for high-performance devices. Richard Stevenson reports.The GaN component market was worth $1.35 billion in 2003 according to [...]
2013-03-21meta-author
PAM-XIAMEN supplies 6 inch c-doped semi-insulating GaAs substrates, which are prime grade and mechanical grade grown by VGF. For wafer details, please view specifications listed below:
1. Prime Grade C-doped Semi-insulating GaAs
PAM220704-GaAs-Un
Parameter
GaAs-Un-6in-625um-PP
UOM
Growth method
VGF
Grade
Prime grade (Epi-ready)
Dopant
C doped
Orientation
(100) ±0.5°
Orientation Angle
N/A
°
Diameter
150.0±0.2
mm
Thickness
625±25 [...]
2022-07-04meta-author
The hexagonal wurtzite GaN nanowires embedded in the nanochannels of anodic alumina membrane were achieved by the direct reaction of Ga vapour with a constant flowing ammonia atmosphere. X-ray diffraction (XRD), scanning electron microscopy and transmission electron microscopy were used to measure the size [...]
2018-12-14meta-author