PAM XIAMEN offers 6″CZ Prime Silicon Wafer
Item7, 50pcs
Silicon wafer:
i. Diameter: 150 mm ± .5 mm,
ii. Thickness: 675μm ±25μm
iii. Doping: P type
iv. Orientation: (100) ± 0.5°
v. TTV: ≤ 5 μm
vi. Bow and Warp: ≤ 20 μm
Growth: CZ
[...]
2020-03-30meta-author
Fabrication of GaN wafers for electronic and optoelectronic devices
The fabrication of GaN wafers from GaN boules (ingots) is described. Gallium nitride boules were grown by hydride vapor phase epitaxy and sliced and sized into wafer blanks. The GaN wafer blanks were lapped and polished. [...]
Indium antimonide (InSb) compound semiconductor, as a direct bandgap semiconductor material, has low electron effective mass, high mobility, and narrow bandgap width. At low temperatures, InSb compound has a high absorption coefficient for infrared light, with a quantum efficiency greater than or equal to 80%. [...]
2024-01-19meta-author
PAM XIAMEN offers 100mm Si wafers. Please send us email at sales@powerwaywafer.com if you need other specs and quantity.
Item
Material
Orient.
Diam
(mm)
Thck
(μm)
Surf.
Resistivity
Ωcm
Comment
PAM2485
p–type Si:B
[100]
4″
3000
P/E
1–100
SEMI Prime, 1Flat, Individual cst, Groups of 7 and 10 wafers
PAM2486
p–type Si:B
[100]
4″
3000
P/E
1–30
SEMI, 2Flats, Individual cst
PAM2487
p–type Si:B
[100]
4″
3175
P/P
1–10
SEMI Prime, 2Flats, Individual cst, TTV<8μm
PAM2488
p–type Si:B
[100]
4″
3175
P/P
1–10
SEMI Prime, 2Flats, Individual cst, [...]
2019-02-19meta-author
Thermal oxides on the Ga-face of low defect density bulk gallium nitride (GaN) were controllably produced under varying conditions and subsequently analyzed. The thermal oxidation was performed in a dry oxygen atmosphere at different temperatures and different oxidation times. Each oxide layer was identified [...]
When talking about the topic that step growth reduces silicon carbide defects, it is necessary to discuss the process for the growth of silicon carbide single crystals. Gas-solid phase transitions are involved in the growth process of silicon carbide single crystals by PVT or HTCVD method. Therefore, there [...]
2021-04-12meta-author