We designed and fabricated AlGaN/GaN high-electron-mobility transistors (HEMTs) employing both a floating gate (FG) and a field plate (FP), which increase the breakdown voltage of AlGaN/GaN HEMTs significantly without sacrificing forward electric characteristics. The electric field strength at the gate–drain region of the proposed AlGaN/GaN HEMT was reduced successfully due to an increase in the number of depletion region edges. The breakdown voltage of the proposed AlGaN/GaN HEMT was 1106 V, while those of the conventional devices with only an FP or FG were 688 and 828 V, respectively. The leakage current of the proposed AlGaN/GaN HEMTs was 1.68 μA under a reverse bias of −100 V while those of the conventional devices with only an FP or FG were 3.21 and 1.91 μA, respectively, under the same condition. The forward electric characteristics of the proposed and conventional AlGaN/GaN HEMTs are similar. The maximum drain current of the proposed AlGaN/GaN HEMTs was 344 mA mm−1 while those of the conventional devices with only an FP or FG were 350 and 357 mA mm−1, respectively. The maximum transconductance of the proposed device was 102.9 mS mm−1, while those of the conventional devices were 97.8 and 101.9 mS mm−1. The breakdown voltage and the leakage current of the proposed device were improved considerably without sacrificing the forward electric characteristics. It should be noted that there were no additional processing steps and mask levels compared to the conventional FP process.
New AlGaN/GaN HEMTs employing both a floating gate and a field plate
Related Posts
(100) Oriented Silicon Wafers-1
PAM XIAMEN offers (100) orientation Silicon Substrates. Below is just a small selection. Let us know if you can use or if we can quote you on another spec. Item Material Orient. Diam (mm) Thck (μm) Surf. Resistivity Ωcm Comment PAM2797 p-type Si:B [100] 4″ 220 ±10 P/E FZ >10,000 SEMI Prime, 1Flat, Empak cst PAM2798 p-type Si:B [100] 4″ 230 ±10 P/E FZ >10,000 SEMI Prime, 1Flat, Empak cst PAM2799 p-type Si:B [100-4° towards[110]] ±0.5° 4″ 525 P/E FZ [...]
Photographic Film
PAM XIAMEN offers Photographic Film. Various Technical Parameters Max plotted area 24″*35″ Thickness 0.18mm Resolution 6000dpi、1200dpi、1600dpi、2500dpi Positioning accuracy ±10μm Repetitive accuracy ±3μm Min Critical Dimension 25μm at 6000 and 12000dpi 12μm at 16000 and 25000dpi CD Tolerance Control ±3μm or ±4μm Main application areas: LCD, PCB, VFD, BGA, FPC and other industries For more information, please visit our website: https://www.powerwaywafer.com, send us email [...]
Silicon Ingots-1
PAM XIAMEN offers Silicon Ingots. Material Description FZ NTD 3″Ø ingot n-type Si:P[111] ±2°, Ro: 50-60 Ohmcm, MCC Lifetime>400μs, (2 ingots: 197mm, 277mm) SEMI FZ 8″Ø ingot n-type Si:P[100] ±2.0°, Ro: 163-174 Ohmcm, MCC Lifetime>14581μs, (1 ingot: 83mm) FZ 6″Ø ingot p-type Si:B[100] ±2.0°, Ro: 1-2 Ohmcm, MCC Lifetime>1777μs, FZ 6″Ø ingot p-type [...]
Magnesium ( Mg ) Single Crystal Substrate
PAM XIAMEN offers Magnesium ( Mg ) Single Crystal Substrate. Magnesium ( Mg ) Single Crystal Substrate , <0001> orn. 5x5x0.9-1.0mm, 1SP Magnesium ( Mg) Polycrystaline Substrate , 10x10x2.0mm, as Cut Magnesium ( Mg) Single Crystal Substrate , <0001> orn. 10x10x0.85-1.0mm, 1SP Magnesium ( [...]
2″ Silicon Wafer-5
PAM XIAMEN offers 2″ Silicon Wafer. Material Orient. Diam. Thck (μm) Surf. Resistivity Ωcm Comment p-type Si:B [100] 2″ 250 P/P 0.01-0.02 SEMI Prime, TTV<5μm p-type Si:B [100] 2″ 300 P/E 0.01-0.02 SEMI, p-type Si:B [100] 2″ 500 P/P 0.01-0.02 SEMI Prime, p-type Si:B [100] 2″ 600 P/E 0.01-0.05 SEMI Prime, p-type Si:B [100] 2″ 525 P/E 0.005-0.020 SEMI Prime, , TTV<5μm p-type Si:B [100] 2″ 300 P/E 0.001-0.005 SEMI Prime, p-type Si:B [100] 2″ 300 P/E 0.001-0.005 SEMI Prime, p-type Si:B [100] 2″ 300 P/E 0.001-0.005 SEMI Prime, p-type Si:B [100] 2″ P/E SEMI Prime p-type Si:B [100] 2″ 525 P/P <0.01 {0.0076-0.0078} SEMI Prime, , in hard cassettes of 5 wafers. p-type Si:B [111] ±0.5° 2″ 275 P/E 1-30 SEMI Prime p-type Si:B [111] ±0.5° 2″ 330 P/E 1-20 SEMI Prime p-type Si:B [111] ±0.5° 2″ 330 P/E 1-20 SEMI Prime p-type [...]
UV light stabilizers market
Fabrication of ZnO nanorod/p-GaN high-brightness UV LED by microwave-assisted chemical bath deposition with Zn(OH)2–PVA nanocomposites as seed layer Chemical solution deposition is a low-temperature and possibly the lowest-cost method of growing ZnO nanorods on a GaN substrate. However, most reported methods leave an interface layer [...]