Gallium oxide (Ga2O3) is a direct ultra wide bandgap semiconductor with a relatively complex structure. Ga2O3 has 5 isomers, namely α、β、γ、ε and δ. These five crystal phases can undergo phase transformation and mutual transformation under certain conditions, among which β- Ga2O3 is the most [...]
2019-04-19meta-author
PAM XIAMEN offers 6″ Silicon Wafer.
Material
Orient.
Diam.
Thck
(μm)
Surf.
Resistivity
Ωcm
Comment
n-type Si:As
[100]
6″
675
OxP/EOx
0.001-0.005
SEMI TEST (spots & minor visual defects), 1Flat (57.5mm), Thermal Oxide 0.1μm±5% thick
p-type Si:B
[100]
6″
735
P/P
FZ >50
Prime, TTV<2μm
p-type Si:B
[100]
6″
650
P/P
FZ 8-13
SEMI Prime (57.5mm)
n-type Si:P
[100]
6″
475
P/P
FZ 60-75
SEMI Prime, MCC Lifetime>14,980μs, Lasermark
n-type Si:P
[112-5° towards[11-1]] ±0.5°
6″
800 ±10
P/P
FZ >3,000
SEMI, 1 JEIDA Flat (47.5mm), TTV<4μm, Lifetime>1,000μs
n-type Si:P
[112-5° towards[11-1]] ±0.5°
6″
950 ±10
P/P
FZ >3,000
SEMI, 1 JEIDA Flat (47.5mm), TTV<4μm, Lifetime>1,000μs
Intrinsic Si:-
[100]
6″
675
P/P
FZ >10,000
SEMI Prime (57.5mm)
Intrinsic Si:-
[100]
6″
675
P/P
FZ >10,000
SEMI [...]
2019-03-04meta-author
PAM XIAMEN offers 2″ Silicon Wafer.
Material
Orient.
Diam.
Thck
(μm)
Surf.
Resistivity
Ωcm
Comment
p-type Si:B
[110] ±0.5°
2″
279
P/E
FZ >1,000
p-type Si:B
[100]
2″
300
P/E
FZ 2,800-3,300
SEMI Prime, TTV<7μm
p-type Si:B
[100]
2″
300
P/E
FZ 2,800-3,300
SEMI Prime, TTV<7μm
p-type Si:B
[100]
2″
300
P/E
FZ 2,800-3,300
SEMI Prime, TTV<7μm
p-type Si:B
[111] ±0.5°
2″
500
P/P
FZ 5,000-6,500
SEMI Test (in unsealed cassette)
p-type Si:B
[111] ±0.5°
2″
275
P/E
FZ 3,000-5,000
SEMI Prime, Lifetime>2,000μs, in hard cassettes of 5 wafers
p-type Si:B
[111-7° towards[110]] ±0.5°
2″
279
P/P
FZ >2,000
SEMI Prime
p-type Si:B
[111] ±0.5°
2″
331
P/E
FZ 2,000-5,000
SEMI, Soft cst
p-type Si:B
[111] ±0.5°
2″
331
P/E
FZ 2,000-5,000
SEMI TEST (Scratched), Soft cst
p-type Si:B
[111] ±0.5°
2″
331
P/E
FZ 2,000-5,000
SEMI [...]
2019-03-07meta-author
This paper describes the bonding characteristics of 3C-SiC wafers using plasma enhanced chemical vapor deposition (PECVD) oxide and hydrofluoric acid (HF) treatment for SiC-on-insulator (SiCOI) structures and high-temperature microelectromechanical system (MEMS) applications. In this work, insulator layers were formed on a heteroepitaxial 3C-SiC film [...]
2015-08-19meta-author
PAM-XIAMEN supplies 6 inch c-doped semi-insulating GaAs substrates, which are prime grade and mechanical grade grown by VGF. For wafer details, please view specifications listed below:
1. Prime Grade C-doped Semi-insulating GaAs
PAM220704-GaAs-Un
Parameter
GaAs-Un-6in-625um-PP
UOM
Growth method
VGF
Grade
Prime grade (Epi-ready)
Dopant
C doped
Orientation
(100) ±0.5°
Orientation Angle
N/A
°
Diameter
150.0±0.2
mm
Thickness
625±25 [...]
2022-07-04meta-author
PAM XIAMEN offers 3″ Silicon Oxide Wafer
3″ Silicon Oxide Wafer
Diameter (mm): 76mm
Grade: Prime
Growth: CZ
Type/Dopant: any
Orientation: 100
Resistivity (Ohm-cm): any
Thickness (µm): 500±25μm
Tolerance (µm): any
Surface Finish: SSP
Flats: SEMI-Std.
TTV < (µm): any
Bow < (µm): any
Warp < (µm): any
Particles [...]