MGO MAGNESIUM OXIDE SINGLE CRYSTAL SUBSTRATE-1

PAM XIAMEN offers MgO Magnesium Oxide Single Crystal.

High quality MgO magnesium oxide crystals are used are used widely for various thin film applications. Customized MgO crystal substrates are available upon request.

1.Specification of MgO Magnesium Oxide Single Crystal

Main Parameters
Growth Method	Special Arc Melting
Crystal Structure	Cubic
Unit cell constant	a = 4.130 Å
Melting point (℃)	2800
Crystal Purity	99.95%
Density	3.58 (g/cm3)
Hardness	5.5 (Mohs)
Thermal Expansion Coefficient, CTE (/℃)	11.2 x 10-6
Crystal Orientation	-100
Optical Transmission	>90% (200~400nm), >98% (500~1000nm)
Dielectric Constants	ε = 9.65
Sizes	10×3 mm, 10×5 mm, 10×10 mm, 15×15 mm, 20×15 mm, 20×20 mm, 30×30 mm
	dia 2” x 0.5mm (2 inch), 3 inch MgO wafer, 4 inch MgO wafer
	Special sizes and orientations are available upon request
Standard Thickness	0.5mm or 1.0mm
Polishing	Single or double side (SSP or DSP)
Crystal orientation	<001> ± 0.5º
Redirection Precision	± 0.5°
Redirection the edge:	2° (special in 1°)
Ra:	≤5Å（5µm×5µm）

MgO Magnesium Oxide Single Crystal.

MgO Magnesium Oxide Single Crystal.

2.Application of MgO Magnesium Oxide Single Crystal

-Growth substrates for high temperature superconducting devices (superconducting quantum devices, CT, communications)
-High temperature and high precision optical materials (aviation, laser processing machine, military, industry)
-Plasma display film (flat panel display, PDP, TV)
-High temperature crucible materials (neutron detection, metallurgical industry)
-Semiconductor materials (substrate, sensor)

For more information, send us email at victorchan@powerwaywafer.com and powerwaymaterial@gmail.com

2019-03-14

Related Posts

Size and distribution of Te inclusions in detector-grade CdZnTe ingots

Size and distribution of Te inclusions in detector-grade CdZnTe ingots To observe the Te inclusions distribution along the axial direction of CdZnTe ingots, batches of as-grown detector-grade CdZnTe crystals grown by vertical Bridgman method, were investigated using IR transmission imaging. However, there is not a [...]

2014-03-28meta-author CdZnTe

4″ Silicon Wafer-13

PAM XIAMEN offers 4″ Silicon Wafer. Material Orient. Diam. Thck (μm) Surf. Resistivity Ωcm Comment n-type Si:Sb [211] ±0.5° 4″ 1,500 ±15 P/P 0.01-0.02 SEMI Prime, TTV<1μm n-type Si:Sb [211] ±0.5° 4″ 1600 C/C 0.01-0.02 SEMI Test, Wafers can be polished for additional fee n-type Si:P [111] 4″ 1200 P/P 35-85 SEMI Prime n-type Si:P [111] ±0.5° 4″ 1500 P/E >20 {24-29} SEMI Prime, TTV<5μm, in Empak cassettes of 2 wafers n-type Si:P [111] ±0.5° 4″ 250 P/E 18-25 SEMI Prime n-type Si:P [111] ±0.5° 4″ 500 P/P 11-15 SEMI Prime, Both-sides Epi Ready polished n-type Si:P [111] 4″ 280 P/E 1.3-2.7 SEMI Prime n-type Si:P [111] ±0.5° 4″ 280 P/E 1.3-2.7 SEMI Prime n-type [...]

2019-03-05meta-author

PbS single crystal

PAM XIAMEN offers PbS single crystal. The sulfate ion is a polyatomic anion with the empirical formula SO2−4 and a molecular mass of 96.06 daltons (96.06 g/mol); it consists of a central sulfur atom surrounded by four equivalent oxygen atoms in a tetrahedral arrangement. [...]

2019-05-14meta-author

4″CZ Prime Silicon Wafer Thickness 525 ± 25 µm-4

PAM XIAMEN offers 4″CZ Prime Silicon Wafer Thickness 525 ± 25 µm. PRIME WAFERS SILICIUM FZ DIAMETER 4’’ (100mm+/-0.5mm) ORIENTATION <1-0-0> +/-1° THICKNESS : 400µm +/-25µm DSP TTV < 10µm – BOW < 40µm FLAT : 32.5mm TYPE P RESISTIVITY : 5000 – 10000 [...]

2019-07-05meta-author

6″ Silicon EPI Wafer

PAM XIAMEN offers 6″ Silicon EPI Wafers. Substrate EPI Comment Size Type Res Ωcm Surf. Thick μm Type Res Ωcm 6″Øx675μm n- Si:P[100] 0.001-0.002 P/EOx 3.2 ±0.2 n- Si:P 0.32-0.46 n+/n++ For more information, please visit our website: https://www.powerwaywafer.com, send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com Found in 1990, Xiamen Powerway Advanced Material Co., Ltd (PAM-XIAMEN) is a leading manufacturer of semiconductor material in China.PAM-XIAMEN develops advanced crystal [...]

2019-03-08meta-author

YSZ crystal-1

PAM XIAMEN offers YSZ （Y2O3 stabilized ZrO2）single crystal wafer. YSZ crystal is grown by “cold crucible” method. It is very difficult to get a larger size YSZ crystal. PAM XIAMEN supplies YSZ crystal wafer up to 2″ diameter. YSZ Substrates (100) 1、Square YSZ (100) [...]

2019-05-21meta-author

Read More

Float-Zone Mono-Crystalline Silicon

PAM-XIAMEN can offer float zone silicon wafer, which is obtained by Float Zone method. Monocrystalline silicon rods is got through float zone growth, and then process the monocrystalline silicon rods into silicon wafers, called float zone silicon wafers. Since the zone-melted silicon wafer is not in contact with the quartz crucible during the floating zone silicon process, the silicon material is in a suspended state. Thereby, it is less polluted during the process of floating zone melting of silicon. The carbon content and oxygen content are lower, the impurities are less, and the resistivity is higher. It is suitable for the manufacture of power devices and certain high-voltage electronic devices.
Read More

Test Wafer Monitor Wafer Dummy Wafer

As a dummy wafer manufacturer, PAM-XIAMEN offers silicone dummy wafer / test wafer / monitor wafer, which is used in a production device to improve safety in the beginning of production process and are used for delivery check and evaluation of process form. As dummy silicon wafers are often used for experiment and test, size and thickness thereof are important factors in most occasions. 100mm, 150mm, 200mm, or 300mm dummy wafer is available.
Read More

Nanofabrication Photoresist

PAM-XIAMEN Offers photoresist plate with photoresist
Read More

Photo Mask

PAM-XIAMEN Offers Photomasks

A photo mask is a thin coating of masking material supported by a thicker substrate, and the masking material absorbs light to varying degrees and can be patterned with a custom design. The pattern is used to modulate light and transfer the pattern through the process of photolithography which is the fundamental process used to build almost all of today’s digital devices.
Read More

CdZnTe (CZT) Wafer

Cadmium Zinc Telluride (CdZnTe or CZT) is a new semiconductor, which enables to convert radiation to electron effectively, it is mainly used in infrared thin-film epitaxy substrate, X-ray detectors and Gamma-ray CdZnTe detectors.
Read More

Ge(Germanium) Single Crystals and Wafers

PAM-XIAMEN offers 2”, 3”, 4” and 6” germanium wafer, which is short for Ge wafer grown by VGF / LEC. Lightly doped P and N type Germanium wafer can be also used for Hall effect experiment. At room temperature, crystalline germanium is brittle and has little plasticity. Germanium has semiconductor properties. High-purity germanium is doped with trivalent elements (such as indium, gallium, boron) to obtain P-type germanium semiconductors; and pentavalent elements (such as antimony, arsenic, and phosphorus) are doped to obtain N-type germanium semiconductors. Germanium has good semiconductor properties, such as high electron mobility and high hole mobility.

sales@powerwaywafer.com tech@powerwaywafer.com

Read More

Float-Zone Mono-Crystalline Silicon

PAM-XIAMEN can offer float zone silicon wafer, which is obtained by Float Zone method. Monocrystalline silicon rods is got through float zone growth, and then process the monocrystalline silicon rods into silicon wafers, called float zone silicon wafers. Since the zone-melted silicon wafer is not in contact with the quartz crucible during the floating zone silicon process, the silicon material is in a suspended state. Thereby, it is less polluted during the process of floating zone melting of silicon. The carbon content and oxygen content are lower, the impurities are less, and the resistivity is higher. It is suitable for the manufacture of power devices and certain high-voltage electronic devices.
Read More

Test Wafer Monitor Wafer Dummy Wafer

As a dummy wafer manufacturer, PAM-XIAMEN offers silicone dummy wafer / test wafer / monitor wafer, which is used in a production device to improve safety in the beginning of production process and are used for delivery check and evaluation of process form. As dummy silicon wafers are often used for experiment and test, size and thickness thereof are important factors in most occasions. 100mm, 150mm, 200mm, or 300mm dummy wafer is available.
Read More

Nanofabrication Photoresist

PAM-XIAMEN Offers photoresist plate with photoresist
Read More

Photo Mask

PAM-XIAMEN Offers Photomasks

A photo mask is a thin coating of masking material supported by a thicker substrate, and the masking material absorbs light to varying degrees and can be patterned with a custom design. The pattern is used to modulate light and transfer the pattern through the process of photolithography which is the fundamental process used to build almost all of today’s digital devices.
Read More

CdZnTe (CZT) Wafer

Cadmium Zinc Telluride (CdZnTe or CZT) is a new semiconductor, which enables to convert radiation to electron effectively, it is mainly used in infrared thin-film epitaxy substrate, X-ray detectors and Gamma-ray CdZnTe detectors.
Read More

Ge(Germanium) Single Crystals and Wafers

PAM-XIAMEN offers 2”, 3”, 4” and 6” germanium wafer, which is short for Ge wafer grown by VGF / LEC. Lightly doped P and N type Germanium wafer can be also used for Hall effect experiment. At room temperature, crystalline germanium is brittle and has little plasticity. Germanium has semiconductor properties. High-purity germanium is doped with trivalent elements (such as indium, gallium, boron) to obtain P-type germanium semiconductors; and pentavalent elements (such as antimony, arsenic, and phosphorus) are doped to obtain N-type germanium semiconductors. Germanium has good semiconductor properties, such as high electron mobility and high hole mobility.