PAM XIAMEN offers 1″ FZ Silicon Ingot with Diameter 25mm
Silicon ingot, per SEMI, G Ø25mm
FZ n-type Si:P[100]±2.0°,
Ro=(1,500-7,000)Ohmcm,
Ground Ingot, NO Flats,
MCC Lifetime>1000µs,
Oxygen<1E16/cc, Carbon<1E16/cc,
Adequately packed, CofC: present.
For more information, send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com
2020-04-26meta-author
After the growth, the silicon carbide single crystal is crystal ingot with surface defects, which cannot be directly used for epitaxy. Therefore, it requires chemical mechanical polishing on silicon carbide. Among the processing skills, spheronization makes the crystal ingot into a standard cylinder; wire [...]
2021-04-02meta-author
PAM XIAMEN offers 4″FZ Prime Silicon Wafer.
Silicon wafers, per SEMI Prime, P/E 4″Ø×525±25μm,
FZ Intrinsic undoped Si:-[111]±0.5°, Ro > 10,000 Ohmcm,
TTV<5μm, Bow<20μm, Warp<30μm,
One-side-Epi-Ready-polished, back-side etched, SEMI Flats,
Sealed in Empak or equivalent cassette,
MCC Lifetime>1,000μs.
For more information, please visit our [...]
2019-07-04meta-author
PAM-XIAMEN offers (11-22) Plane U-GaN Freestanding GaN Substrate
Item
PAM-FS-GAN(11-22)- U
Dimension
380+/-50um
Thickness
350 ±25 µm 430 ±25 µm
Orientation
(11-22) plane off angle toward A-axis 0 ±0.5°
(11-22) plane off angle toward C-axis -1 ±0.2°
Conduction Type
N-type / Undoped
Resistivity (300K)
< 0.1 Ω·cm
TTV
≤ 10 µm
BOW
BOW ≤ 10 µm
Surface Roughness
Front side: Ra<0.2nm, epi-ready;
Back side: Fine Ground or polished.
Dislocation Density
≤ 5 x 10 6cm-2
Macro Defect Density
0 cm-2
Useable Area
> 90% (edge exclusion)
Package
each in single wafer container, under nitrogen atmosphere, packed in class 100 clean room
For more information, please contact us email at victorchan@powerwaywafer.com and powerwaymaterial@gmail.com
2020-08-20meta-author
PAM XIAMEN offers YVO4 Undoped Yttrium Orthovanadate Crystals.
UNDOPED YVO4 IS AN EXCELLENT NEWLY DEVELOPED BIREFRINGENCE OPTICAL CRYSTAL.
It has very good transmission in a wide wavelength range from visible to infrared.
It has large index of refractivity and birefringence difference.
Compared with other important birefringence crystals, YVO4 has higher. [...]
2019-03-18meta-author
PAM XIAMEN offers 2″ Prime Silicon Wafer Tnickness 675 +/- 20 microns.
Wafers 2 inches in diameter of monocrystalline silicon with an insulating oxide.
2 inches in diameter
The silicon substrate
orientation<100>
resistivity>10Ωcm
The insulating thermal oxidation film thickness 300nm
Polishing: one-sided for microelectronics [...]