PAM XIAMEN offers Glass Substrates(ITO Coated Glass / Plastic Substrates and ITO/ZnO coated Sodalime Glass).

ITO Coated Glass / Plastic Substrates

ITO coated(sodalime) glass has highly electrical conductivity yet with excellent transparence. It has been widely used in flat panel display and solar cells.

                      ITO  Physical properties
Melting point 1800–2200 K (1526-1926 °C) (2800–3500 °F)
Density 7120–7160 kg/m3 at 293 K
Color (in powder form) Pale yellow to greenish yellow, depending on SnO2 concentration
Values vary with composition. SI units and STP are used except where noted.

ITO Coated Glass, 10mmx10mmx 0.7mm
ITO Coated Glass, 1″ x1″
ITO Coated Glass, 1″ x3″x 0.7mm\
ITO Coated Glass, 100mm x100mm x 0.7mm
ITO Coated Glass,2″x 0.7mm
ITO Coated Plastic Film
ITO Film on Corning 7980

ITO/ZnO coated Sodalime Glass

ITO/ZnO Coated Glass Substrate 1″ x 1″ x 0.7 mm, ITO Film=100nm, ZnO film=50nm

For more information, please visit our website: https://www.powerwaywafer.com,
send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com

Found in 1990, Xiamen Powerway Advanced Material Co., Ltd (PAM-XIAMEN) is a leading manufacturer of semiconductor material in China. PAM-XIAMEN develops advanced crystal growth and epitaxy technologies, manufacturing processes, engineered substrates and semiconductor devices. PAM-XIAMEN’s technologies enable higher performance and lower cost manufacturing of semiconductor wafer.

Quality is our first priority. PAM-XIAMEN has been ISO9001:2008, owns and shares four modern facories which can provide quite a big range of qualified products to meet different needs of our customers, and every order has to be handled through our rigorous quality system.Test report is provided for each shipment, and each wafer are warranty.

2019-04-18

Share this post

Related Posts

InP/InGaAs/InP epi wafer

When the In composition in the InGaAs material reaches 0.53, and Ga reaches 0.47, InGaAs / InP lattice matched makes it can form a heterojunction. The InGaAs / InP heterojunction structure utilizes the steps of the conduction band and valence band formed by the [...]

2013-11-13meta-author
Blue GaN LD Wafer

PAM-XIAMEN can offer 2” InGaN/GaN quantum well blue laser diode wafer on sapphire or silicon substrate as follows. The blue GaN LD wafer for commercial applications illustrates the great potential of III-V epitaxial wafers. 1. Specification of 440-460nm Blue GaN LD wafer  PAM190909-GAN-LD Item Descriptions Materials Substrate blue laser 440-460nm InGaN 2 inch Sapphire substrate*** GaN Blue LD EPI Wafer Spec  Spec LD Epitaxial Wafer Size Growth MOCVD Diameter 50.8 ± 0.2 [...]

2018-08-22meta-author
Distribution of Te inclusions in a CdZnTe wafer and their effects on the electrical properties of fabricated devices

We quantified the size and concentration of Te inclusions along the lateral- and the growth-directions of a ∼6 mm-thick wafer cut axially along the center of a CdZnTe ingot. We fabricated devices, selecting samples from the center slice outward in both directions, and then [...]

2015-12-11meta-author
V-shaped defects in InGaN/GaN multiquantum wells

V-shaped defects in InGaN/GaN multiquantum wells InGaN/GaN multiquantum well (MQW) structures have been grown on (0001) sapphire substrate by metalorganic chemical vapor deposition. From cross-sectional transmission electron microscopy (TEM), a number of V-shaped defects has been observed on the surface which are associated with mixed [...]

2014-01-24meta-author
Indium Arsenide Ingot with Zinc Blende Structure Grown By VGF

PAM-XIAMEN provides indium arsenide (InAs) ingot with high quality and competitive price. Indium arsenide is a group III-V compound semiconductor material composed of indium and arsenic. It is a silver-gray solid at room temperature, and the indium arsenide crystal structure is a zinc blende crystal [...]

2021-06-23meta-author
AlN Thin Film for FBAR and SAW

AlN (aluminum nitride) is a covalent bond compound with a hexagonal wurtzite structure. Usually gray or grayish white in color, it has advantages such as high thermal conductivity, high-temperature insulation, good dielectric properties, high material strength at high temperatures, and low coefficient of thermal [...]

2024-03-13meta-author