PAM XIAMEN offers PbSe single crystal substrate.

Lead selenide (PbSe), or lead(II) selenide, a selenide of lead, is a semiconductor material. It forms cubic crystals of the NaCl structure; it has a direct bandgap of 0.27 eV at room temperature. (Note that incorrectly identifies PbSe and other IV–VI semiconductors as indirect gap materials.) It is a grey crystalline solid material.

It is used for manufacture of infrared detectors for thermal imaging, operating at wavelengths between 1.5–5.2 µm. It does not require cooling, but performs better at lower temperatures. The peak sensitivity depends on temperature and varies between 3.7–4.7 µm.

Single crystal nanorods and polycrystalline nanotubes of lead selenide were synthesized via controlled organism membranes. The diameter of the nanorods is approx. 45 nm and their length is up to 1100 nm, for nanotubes the diameter is 50 nm and the length up to 2000 nm.

Lead selenide nanocrystals embedded into various materials can be used as quantum dots, for example in nanocrystal solar cells.

The mineral clausthalite is a naturally occurring lead selenide.

It may be formed by direct reaction between its constituent elements

General Properties:
Crystal Structure:  Halite (cubic), cF8
Molar mass:         286.16 g/mol
Melting point:      1078 °C, 1351 K, 1972 °F

PbSe (100) Purity :99.999% N type, 10x10x1.0 mm, 2sp(60/40)

PbSe (100) N type, 10x10x0.5 mm, 2sp

PbSe (100) N type, 5x5x0.5 mm, 2sp

PbSe (111) Purity 99.999% N type, 10x10x1.0 mm, 2sp(60/40)

PbSe (100) N type, , 25.4 mm in dia x1.0 mm, un-polished

 

Due to the rapid changes in the semiconductor wafer market and our production lines, our supply capacity will change with it, but the changes will not be shown on our website. So we reserve the right to explain all the information on our website.

For more information, please visit our website: https://www.powerwaywafer.com,
send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com

Found in 1990, Xiamen Powerway Advanced Material Co., Ltd (PAM-XIAMEN) is a leading manufacturer of semiconductor material in China. PAM-XIAMEN develops advanced crystal growth and epitaxy technologies, manufacturing processes, engineered substrates and semiconductor devices. PAM-XIAMEN’s technologies enable higher performance and lower cost manufacturing of semiconductor wafer.

You can get our free technology service from enquiry to after service based on our 25+ experiences in semiconductor line.

2019-05-14

Share this post

Related Posts

4″ FZ Intrinsic Silicon Wafer DSP

PAM XIAMEN offers 4″ FZ Intrinsic Silicon Wafer DSP 4″ FZ (100) intrinsic, DSP wafer Si FZ (100) dia 4’’ x 525µm intrinsic R > 20,000 ohm.cm 2 sides polished with SEMI Std flats Roughness<0.5nm For more information, send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com

2021-03-17meta-author
2″ Silicon Wafer-6

PAM XIAMEN offers 2″ Silicon Wafer. Material Orient. Diam. Thck (μm) Surf. Resistivity Ωcm Comment p-type Si:B [111] 2″ 1000 P/E 0.001-0.005 SEMI Prime p-type Si:B [111] ±0.5° 2″ 500 P/P <0.01 SEMI Prime p-type Si:B [111] ±0.5° 2″ 500 P/P <0.01 {0.00087-0.00100} SEMI Prime p-type Si:Ga Poly. 2″ C/C 0.024-0.036 Gallium doped Concentrate (each with measured Gallium content) n-type Si:P [110] 2″ 280 P/E 19-33 SEMI Prime, 1 Flat @ [1,-1,0], in hard cst n-type Si:P [110] 2″ 280 P/E 19-33 SEMI Prime, n-type Si:P [110] ±0.5° 2″ 300 P/E 1-5 SEMI Prime, , TTV<5μm n-type Si:Sb [110] 2″ 375 P/E 0.005-0.020 SEMI n-type Si:Sb [110] 2″ 375 P/E 0.005-0.020 SEMI n-type Si:P [100] 2″ 400 P/P 210-880 SEMI Prime, n-type Si:P [100] 50mm 280 P/E 130-280 SEMI Prime, n-type Si:P [100] 2″ 300 P/P 33-48 SEMI TEST [...]

2019-03-07meta-author
Growth of 3C–SiC films on Si substrates by vapor–liquid–solid tri-phase epitaxy

Growth of 3C–SiC films on Si substrates by vapor–liquid–solid tri-phase epitaxy Cubic SiC films (3C–SiC) were deposited on (111) Si substrates by a vapor–liquid–solid tri-phase growth method. In such a process a thin copper layer, which was evaporated on the Si substrate prior to the [...]

2015-05-07meta-author , ,
Portable Diagnostic Spectrum Analyzer

PSA-01 is a portable nuclear spectrum acquisition instrument, which integrates main amplifier，multi-channel pulse analyzer and high-voltage. Its gain, high-voltage and shaping time are adjustable. With upper computer software, it can acquit nuclear spectrum, analyzing, processing and storage data. Its built-in Li-battery could charge more [...]

2019-04-25meta-author
YVO4 UNDOPED YTTRIUM ORTHOVANADATE CRYSTAL

PAM XIAMEN offers YVO4 Undoped Yttrium Orthovanadate Crystals. UNDOPED YVO4 IS AN EXCELLENT NEWLY DEVELOPED BIREFRINGENCE OPTICAL CRYSTAL. It has very good transmission in a wide wavelength range from visible to infrared. It has large index of refractivity and birefringence difference. Compared with other important birefringence crystals, YVO4 has higher. [...]

2019-03-18meta-author
Non-destructive evaluation of the strain distribution in selected-area He+ ion irradiated 4H-SiC

We are an expert of semiconductor wafers in semiconductor industry, and we offer technology support and wafers selling for thousands    of univerisities and industrial customers by our decades experience, including Cornell University, Stanford Univeristy,Peking University,      Shandong Univerity, university of south carolina,Caltech Faraon lab (USA）,University of California, Irvine (USA),Singapore MIT Alliance    for Research and Technology Centre (SMART),West Virginia University,Purdue Univerity, University of California, Los Angeles,King Abdullah University of Science & Technology,Massachusetts Institute of Technology,University of Houston,University of Wisconsin,University of    Science and Technology of China etc. And now we show one article example as follows, who bought our wafers or service: Article title: Non-destructive evaluation of the strain distribution in selected-area He+ ion irradiated 4H-SiC Published by: Subing Yang;Sakiko Tokunaga;Minako Kondo;Yuki Nakagawa;Tamaki Shibayama; a Graduate School of [...]

2019-12-02meta-author