PAM XIAMEN offers 8″ Prime Silicon Wafer.
Silicon wafers, per SEMI Prime,
P/E 8″(200.0±0.2mm) Ø×1,000±25µm,
p-type Si:B[111]±0.5°, Ro: <100 Ohmcm,
TTV<6µm, Bow<60µm, Warp<60µm,
One-side-polished, Particles: ≤10@≥0.3µm,
Back-side etched, SEMI notch,
Sealed in Empak or equivalent cassette.
For more information, please visit our website: https://www.powerwaywafer.com, [...]
2019-07-02meta-author
PAM-XIAMEN can offer 2” InGaAs/InP epi wafer for PIN as follows. InGaAs is the compound of InAs and GaAs. In the periodic table of chemical elements, In and Ga are elements of the third group, and As is the fifth group element. The properties of InGaAs [...]
PAM XIAMEN offers 4″ Silicon Wafer.
Material
Orient.
Diam.
Thck
(μm)
Surf.
Resistivity
Ωcm
Comment
Intrinsic Si:-
[100]
4″
500
P/E
FZ 13,000-20,000
SEMI Prime, TTV<5μm, Front-side Prime polish, Back-side light polish
Intrinsic Si:-
[100]
4″
615 ±10
C/C
FZ >10,000
SEMI Prime
Intrinsic Si:-
[100]
4″
800
C/C
FZ >10,000
SEMI Prime
Intrinsic Si:-
[111] ±0.5°
4″
525
P/E
FZ >22,000
SEMI Prime
Intrinsic Si:-
[111] ±0.5°
4″
300
P/E
FZ 20,000-40,000
SEMI, TTV<5μm
Intrinsic Si:-
[111] ±0.5°
4″
450
P/P
FZ >20,000
SEMI Prime
Intrinsic Si:-
[111] ±0.5°
4″
500
P/E
FZ >20,000
SEMI Prime, Extra 3 free non-prime wafers included with 4 prime wafers
Intrinsic Si:-
[111] ±1.0°
4″
500
P/P
FZ >15,000
SEMI Prime, TTV<5μm
p-type Si:B
[110] ±0.25°
4″
525
P/E
5-10
SEMI [...]
2019-03-05meta-author
PAM XIAMEN offers 2″ Silicon Wafer.
Diameter
(mm)
Type
Dopant
Growth
method
Orientation
Resistivity
Thickness
Surface
Grade
50.8
N
Phos
FZ
(111) Off 2″ Towards (110)
2k-5k
350-400
P/E
PRIME
50.8
N
Phos
CZ
-100
1-20
10-30
P/P
PRIME
50.8
N
Phos
CZ
-100
1-20
40-60
P/P
PRIME
50.8
N
Phos
CZ
-100
1-20
80-100
P/P
PRIME
50.8
N
Phos
CZ
-100
1-20
140-160
P/P
PRIME
50.8
N
Phos
FZ
-100
>1000
200-500
P/E
PRIME
50.8
N
Phos
FZ
-100
>1000
200-500
P/P
PRIME
50.8
N
Phos
CZ
-100
225-275
P/P
PRIME
50.8
N
Phos
FZ
-100
>3000
225-275
P/P
PRIME
50.8
N
As
CZ
-100
.001-.005
250-300
P/E
PRIME
50.8
N
Sb
CZ
-100
.005-.02
250-300
P/P
PRIME
50.8
N
Phos
FZ
-100
>3000
250-300
P/E
PRIME
50.8
N
Phos
CZ
-100
1-20
250-300
P/E
PRIME
50.8
N
Phos
CZ
-100
1-20
250-300
P/E/DTOx
PRIME
50.8
N
Phos
CZ
-100
1-20
250-300
P/E/Ni
PRIME
50.8
N
Phos
CZ
-100
1-20
250-300
P/E/WTOx
50.8
N
Phos
FZ
-100
2000-5000
275-325
P/P
PRIME
50.8
N
Phos
CZ
-100
450-500
P/P
PRIME
50.8
N
Phos
CZ
-100
43485
500-550
P/E
PRIME
50.8
N
Phos
CZ
-100
1000-1050
P/E
PRIME
50.8
N
Phos
CZ
-100
1-20
2900-3100
P/E
PRIME
For more information, please visit our website: https://www.powerwaywafer.com,
send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com
Found in 1990, Xiamen Powerway Advanced Material Co., Ltd (PAM-XIAMEN) is a leading manufacturer of semiconductor material in China.
PAM-XIAMEN develops advanced crystal [...]
2019-02-27meta-author
PAM XIAMEN offers Zero Diffraction Plate.
SiO2 Single Crystal Zero Diffraction Plate for XRD
Desktop X-Ray Orientation Machine for Single Crystal Orientation Measurement
Zero Diffraction Plate for XRD sample: 30 x 30 x 2.5 mm with Cavity 10 ID x 1.0 mm, 2sp, SiO2 [...]
2019-05-22meta-author
PAM XIAMEN offers 3″CZ Prime Silicon Wafer-1
Item4, 50pcs
Silicon wafer:
i. Diameter: 76.2 mm ± 0.5 mm,
ii. Thickness: 375μm ± 25μm
iii. Doping: N type
iv. Orientation: (100) ± 0.5°
v. TTV: ≤ 5 μm
vi. Bow and Warp: ≤ 20 μm
Growth: [...]
2020-03-27meta-author