PAM XIAMEN offers 4″ Silicon Wafer.
Material
Orient.
Diam.
Thck
(μm)
Surf.
Resistivity
Ωcm
Comment
p-type Si:B
[100]
4″
480
C/C
1-30
SEMI Test, UNPOLISHED WAFERS WITH EDGE CHIPS
p-type Si:B
[100]
4″
500
P/P
1-50
SEMI Prime, Carbon content (0.2-0.9)E16/cc per ASTM F1319, Oxygen content (9.4-8.8)E17/cc
p-type Si:B
[100]
4″
500
P/P
1-50
SEMI Prime, Carbon content ~1.0ppma
p-type Si:B
[100]
4″
500
P/P
1-50
SEMI Prime, Carbon content ~0.2ppma
p-type Si:B
[100]
4″
500
P/P
1-50
SEMI Prime, Carbon content (1.3-2.2)E16/cc per ASTM F1319, Oxygen content (7.9-7.7)E17/cc
p-type Si:B
[100]
4″
500
P/P
1-50
SEMI [...]
2019-03-05meta-author
PAM XIAMEN offers 6″ FZ Silicon Ingot with Diameter 150.7±0.3mmØ
Silicon ingot, per SEMI, G 150.7±0.3mmØ
FZ p-type Si:B[110]±2.0°
Ro > 1,000 Ohmcm
Ground Ingot
NO Flats
NOTE: Oxygen<1E16/cc, Carbon<1E16/cc
MCC Lifetime>1,000µs
For more information, send us email at sales@powerwaywafer.com and powerwaymaterial@gmail.com
2020-06-10meta-author
The PN junction material has a single conductivity, which is a characteristic utilized by many devices in electronic technology, such as semiconductor diodes and bipolar transistors. PAM-XIAMEN can offer silicon PN junction wafers. Here we just list a specific epitaxial structure of photodiode application for your reference. More silicon epitaxial [...]
2023-09-28meta-author
PAM-XIAMEN can offer 2” InGaAs/InP epi wafer for PIN as follows. InGaAs is the compound of InAs and GaAs. In the periodic table of chemical elements, In and Ga are elements of the third group, and As is the fifth group element. The properties of InGaAs [...]
Progress in bulk GaN growth*
Three main technologies for bulk GaN growth, i.e., hydride vapor phase epitaxy (HVPE), Na-flux method, and ammonothermal method, are discussed. We report our recent work in HVPE growth of GaN substrate, including dislocation reduction, strain control, separation, and doping of [...]
2018-05-29meta-author
The long-wavelength InGaAsN quantum well laser based on GaAs substrate is one of the most promising development directions. InGaAsN laser structures are usually grown by molecular beam epitaxy (MBE) or metal organic vapor deposition (MOCVD). InGaNAs material is a promising material for long wavelength [...]